China Mechanical Engineering ›› 2022, Vol. 33 ›› Issue (12): 1493-1503.DOI: 10.3969/j.issn.1004-132X.2022.12.011

Previous Articles     Next Articles

Association between Wear Resistance of TiVN Coatings and Their Cutting Performance

FAN Qingbo1;YANG Fan1;GUAN Xiaoyan2;LI Hao1;FAN Xiaoqiang1;ZHU Minhao1   

  1. 1.School of Materials Science and Engineering,Southwest Jiaotong University,Chengdu,610031
    2.School of Materials and Chemical Engineering,Zhongyuan University of Technology,Zhengzhou,450007
  • Online:2022-06-25 Published:2022-07-07

TiVN涂层的耐磨性与切削性能的关联研究

范庆波1;杨帆1;关晓艳2;李浩1;樊小强1;朱旻昊1   

  1. 1.西南交通大学材料科学与工程学院,成都,610031
    2.中原工学院材料与化工学院,郑州,450007
  • 通讯作者: 李浩(通信作者),男,1990年生,博士、副教授。研究方向为减摩耐磨材料。E-mail:lihao@swjtu.edu.cn。
  • 作者简介:范庆波,男,1993年生,硕士研究生。研究方向为硬质耐磨涂层、摩擦磨损。E-mail:2670351693@qq.com。
  • 基金资助:
    国家自然科学基金(51805557);四川省科技计划(2019YFSY0012)

Abstract: TiN and TiVN coatings were prepared by multi-arc ion deposition technology, and the tribological and cutting performance of the coatings at different conditions were compared, then the main factors affecting the service performance of tool coatings were pointed out. The experimental results show that V doping may effectively improve the hardness and bonding forces of TiN coatings, and reduce the friction factor and wear rate of TiN coatings at low temperature. However, the TiVN coatings have a higher wear rate when the temperature is higher than 500 ℃, and this is ascribed to the easy oxidation of V. The cutting tests show that TiN and TiVN coatings flake easily on the main cutting edges and transverse edge areas of the twist drills, whilst, there is no significant peeling of the coatings on flank surfaces of the cutting tools. It is supposed that the excellent cutting performance of TiVN coatings is ascribed to the high bonding strength and wear resistance. The service performance of the tool coatings is related to the wear resistance and bonding strength. In addition, the main cutting edges and chisel edge areas of the tools have strict requirements on the wear resistance and bonding strength. Meanwhile, the temperature of the cutting edge tips is high, which shows a high requirement for  high temperature wear resistances and bonding strength of the coatings.

Key words: multi-arc ion plating, TiN coating, TiVN coating, friction and wear, cutting performance

摘要: 通过多弧离子镀沉积技术制备了TiN和TiVN涂层,对比了两种涂层在不同工况下的摩擦磨损性能和切削性能,并指出影响刀具涂层服役性能的主要因素。结果表明,V元素掺杂有效提高了TiN涂层的硬度和结合力、减小了TiN涂层的摩擦因数和低温下的磨损率,但V容易氧化的特性导致500 ℃及以上温度TiVN涂层产生较高的磨损率。切削测试表明,在麻花钻的主切削刃和横刃区域两种涂层发生明显的剥落,而在后刀面涂层未发生明显剥落,TiVN涂层较高的膜基结合强度和耐磨性能使得它对刀具的防护效果更佳;刀具涂层的服役性能与其耐磨性能和膜基结合强度有关,刀具的主切削刃和横刃区域对涂层的耐磨性能和膜基结合强度有着苛刻的要求,且切削刃尖端温度较高,对涂层的高温耐磨性能和膜基结合强度要求也高。

关键词: 多弧离子镀, TiN涂层, TiVN涂层, 摩擦磨损, 切削性能

CLC Number: