Intrinsic Dissipation in Low Cycle Fatigue for Stainless Steel Weldments

doi:10.3969/j.issn.1004-132X.2020.17.005

Abstract

Abstract: DIC and infrared thermography(IRT) were used to measure the deformation and surface temperature fields during low cycle fatigue of 310S with welded joints. DIC was used to observe the nonuniformity of local deformations of the welded joints. IRT provided the temperature field distribution of sample surfaces. The test results show that in high stress areas, fatigue failure occurs mostly in the welded joints; in the low stress areas, fatigue failure occurs mostly in base metal areas. The intrinsic dissipation distribution of specimen surfaces may be acquired by solving the local thermal diffusion equation, which may be used to predict the crack initiation positions.

Key words: stainless steel, welded joint, fatigue, dissipation, digital image correlation(DIC)

摘要：

采用数字图像相关(DIC)技术和红外热成像技术测量了310S不锈钢焊接接头低周疲劳过程中的变形和表面温度场，其中，DIC技术用于观察焊接接头局部变形的不均匀性，红外热成像技术提供样品表面的温度场分布。结果表明：在高应力区域，疲劳失效主要发生在焊接接头处；在低应力区域，疲劳失效主要发生在母材区。通过求解局部热扩散方程计算获得的试件表面的固有耗散分布可用于预测裂纹萌生位置。

关键词: 不锈钢, 焊接接头, 疲劳, 耗散, 数字图像相关

CLC Number:

O346.2

HAO Zhiyan;HUANG Zhiyong;WANG Qingyuan. Intrinsic Dissipation in Low Cycle Fatigue for Stainless Steel Weldments[J]. China Mechanical Engineering, DOI: 10.3969/j.issn.1004-132X.2020.17.005.

郝智彦;黄志勇;王清远. 不锈钢焊接件低周疲劳固有耗散分析[J]. 中国机械工程, DOI: 10.3969/j.issn.1004-132X.2020.17.005.

References

[1]寇宏滨，邱荣英，朱剑峰. 轿车用薄板焊接结构疲劳性能研究[J]. 中国机械工程, 2014，25(15)： 2107-2111.
KOU Hongbin，QIU Rongying，ZHU Jianfeng. Study on Fatigue Property of Auto Seam Welded Thin-sheet Structures[J]. China Mechanical Engineering，2014, 25(15)：2107-2111.
[2]GENG C J，WU B L，DU X H，et al. Low Cycle Fatigue Behavior of Extruded AZ31B Magnesium Alloy[J]. Transactions of Nonferrous Metals Society of China，2013，23(6)：1589-1594.
[3]CHRYSOCHOOS A，BOULANGER T，MORABITO A E. Dissipation and Thermoelastic Coupling Associated with Fatigue of Materials[M]//FRMOND M, MACERI F. Mechanics，Models and Methods in Civil Engineering. Berlin: Springer，2012：147-156.
[4]MENEGHETTI G. Analysis of the Fatigue Strength of a Stainless Steel Based on the Energy Dissipation[J]. International Journal of Fatigue，2007，29(1)：81-94.
[5]李源，韩旭，刘杰，等. 一种基于耗散能计算的高周疲劳参数预测方法[J]. 力学学报，2013，45(3)：367-374.
LI Yuan，HAN Xu，LIU Jie，et al. A Prediction Method on High-cycle Fatigue Parameters Based on Dissipated Energy Computation[J]. Chinese Journal of Theoretical and Applied Mechanics，2013，45(3)：367-374.
[6]WANG H，JING H，ZHAO L，et al. Uniaxial Ratcheting Behaviour of 304L Stainless Steel and ER308L Weld Joints[J]. Materials Science and Engineering: A，2017，708：21-42.
[7]YUAN X，YU W，FU S，et al. Effect of Mean Stress and Ratcheting Strain on the Low Cycle Fatigue Behavior of a Wrought 316LN Stainless Steel[J]. Materials Science and Engineering: A，2016，677：193-202.
[8]DAS A. Cyclic Plasticity Induced Transformation of Austenitic Stainless Steels[J]. Materials Characterization，2019，149：1-25.
[9]MENEGHETTI G. Analysis of the Fatigue Strength of a Stainless Steel Based on the Energy Dissipation[J]. International Journal of Fatigue，2007，29(1)：81-94.
[10]HUANG Z Y，LIU H Q，WANG C，et al. Fatigue Life Dispersion and Thermal Dissipation Investigations for Titanium Alloy TC17 in Very High Cycle Regime[J]. Fatigue & Fracture of Engineering Materials & Structures，2015，38(11)：1285-1293.
[11]HUANG Z Y，WANG Q Y，WAGNER D，et al. A Very High Cycle Fatigue Thermal Dissipation Investigation for Titanium Alloy TC4[J]. Materials Science and Engineering: A，2014，600：153-158.
[12]GUO Q，GUO X. Research on High-cycle Fatigue Behavior of FV520B Stainless Steel Based on Intrinsic Dissipation[J]. Materials & Design，2015，90(4)：248-255.

[1]	TAO Yun-Ping, WANG Zhi-Yuan. Energy Dissipation of Bolt Joint under Cycle Load and Parameter Identification of Interfaces  [J]. J4, 201016, 21(16): 1941-1943,1951.
[2]	LI Yanle, PAN Zhongtao, QI Xiaoxia, CUI Weiqiang, CHEN Jian, LI Fangyi. Effect of Heat Treatment on Temperature and Stress Distribution during Laser Cladding of 316L Steels [J]. China Mechanical Engineering, 2024, 35(04): 666-677.
[3]	WU Zhongrui, CHEN Difa, WU Jizhan, YANG Yudian, LIU Huaiju. Study on Influences of Ni Content, Nitriding Hardening Depth, and Shot Peening on Bending Fatigue Performance of 42CrMo Gears [J]. China Mechanical Engineering, 2024, 35(03): 394-404.
[4]	YAO Lingyun, LIN Yongjie, LI Li, . Accelerated Editing of Automotive Component Load Spectrum Based on S-transform Dual Threshold Method [J]. China Mechanical Engineering, 2024, 35(02): 215-220.
[5]	WU Ruo, WEI Peitang, XIE Huaijie, BIAN Jiang, LU Zehua, LIU Huaiju. Contact Fatigue Performance of PEEK under Oil-injected Lubrication [J]. China Mechanical Engineering, 2024, 35(02): 221-228.
[6]	SHEN Minmin, SHI Rui, GUO Pengfei, YANG Yang, YANG Xiaodong, YANG Jihou. Study on Vibration and Fatigue of Distributed Connection Structures of Reusable Aircrafts [J]. China Mechanical Engineering, 2024, 35(01): 45-55.
[7]	CUI Haitao, QIAN Chunhua. Research on Thermo-mechanical Fatigue Life Prediction Model of Ni-base Superalloy [J]. China Mechanical Engineering, 2024, 35(01): 67-73,82.
[8]	GOU Ruijie, ZHANG Xiaofeng, ZHANG Hongbin, YAO Jun, LI Xun. Effects of Tool Wear on Milling Surface Integrity and Fatigue Properties of Allvac 718Plus Superalloy [J]. China Mechanical Engineering, 2023, 34(24): 2920-2926.
[9]	YANG Wenjun, PANG Jianchao, KANG Xin, WANG Lei, LI Sicheng, ZHANG Zhefeng. Thermo-mechanical Fatigue Life Prediction and Optimization Design Method Based on Equivalent Component Model of Cylinder Head [J]. China Mechanical Engineering, 2023, 34(24): 3004-3014.
[10]	WU Zhifeng, GAO Jianxiong, XU Rongxia, ZHU Pengnian. A Non-uniform Damage Accumulation Model Considering Load Interactions [J]. China Mechanical Engineering, 2023, 34(22): 2659-2664，2673.
[11]	WANG Wei, JI Xiaogang, FANG Chuang, NIU Guofa. Fatigue Life Prediction of Flexible Lattice Structures Prepared by Digital Light Process [J]. China Mechanical Engineering, 2023, 34(21): 2637-2645.
[12]	GUO Wei, CAO Hongrui, ZI Yanyang, WEI Xunkai. Study on Contact Fatigue Crack Modeling and Propagation Law of Rolling Bearings [J]. China Mechanical Engineering, 2023, 34(16): 1891-1899.
[13]	CAO Leilei, KANG Fanjun, GUO Chengchen, SONG Xuding, LYU Wenche. Multi-axis Fatigue Life Analysis Method for Welded Structures of Transmission Intermediate Shafts [J]. China Mechanical Engineering, 2023, 34(13): 1605-0610,1627.
[14]	WANG Shoucai, SUN Ang, LIU Rugang. Numerical Simulation and Experimental Verification of Pulling-riveting Process of New Non-plate Nuts [J]. China Mechanical Engineering, 2023, 34(07): 875-881.
[15]	ZHOU Xin, LEI Xianqing, LI Geqiang. Energy Regeneration Assistance of Soft Braking and Corresponding Thermal Dissipation Management System [J]. China Mechanical Engineering, 2023, 34(06): 746-755.