China Mechanical Engineering ›› 2022, Vol. 33 ›› Issue (12): 1468-1476.DOI: 10.3969/j.issn.1004-132X.2022.12.008

Previous Articles     Next Articles

Environmental Adaptability and Tribological Properties of MoS2/WS2 Composite Films

FAN Xin1,2;REN Siming1; WANG Haixin1 ;PU Jibin1   

  1. 1.Key Laboratory of Marine Materials and Related Technologies,Zhejiang Key Laboratory of Marine Materials and Protective Technologies,Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences,Ningbo,Zhejiang,315201
    2.University of Chinese Academy of Sciences,Beijing,100049
  • Online:2022-06-25 Published:2022-07-07



  1. 1.中国科学院宁波材料技术与工程研究所,浙江省海洋材料与防护技术重点实验室,中国科学院海洋新材料与应用技术重点实验室,宁波,315201
  • 通讯作者: 蒲吉斌(通信作者),男,1979年生,研究员、博士研究生导师。研究方向为极端环境新型功能防护涂层。。
  • 作者简介:范昕,女,1997年生,硕士研究生。研究方向为材料损伤及表面防护。。
  • 基金资助:

Abstract: The hot and humid atmosphere had a serious deteriorating effect on the tribological properties of the MoS2 lubricating films. Unbalanced magnetron sputtering technology was successfully used to prepare WS2 doped MoS2 composite films, and the addition of a small amount of WS2 in the MoS2 matrix might induce the preferential growth of MoS2 along the(002) crystal planes, the film structure became denser, the penetration and diffusion of corrosive media were significantly inhibited, and the MoS2/WS2 composite film exhibited high salt spray corrosion resistance, low friction coefficient and wear rate. The composition-optimized MoS2-1.6at.%WS2 composite film was only oxidized on the surface layers after 4 days of salt spray, and still maintained a low friction coefficient of 0.16 and a low wear rate of 3.80×10-6 mm3/(N·m). 

Key words:  , MoS2/WS2 composite film, salt spray environment, corrosion resistance, tribological property

摘要: 湿热大气环境对MoS2润滑薄膜的摩擦学性能有严重的劣化作用。采用非平衡磁控溅射技术成功制备了WS2掺杂MoS2复合薄膜,研究发现,MoS2基体中掺入少量WS2可以诱导MoS2沿(002)晶面择优生长,薄膜结构变得更加致密,显著抑制腐蚀介质的渗透和扩散,使MoS2/WS2复合薄膜展现出高盐雾耐蚀性、小摩擦因数和低磨损率。成分优化的MoS2-1.6%WS2(原子分数)复合薄膜在经历4天的盐雾试验后仅表层被氧化,仍能保持0.16的小摩擦因数和3.80 × 10-6 mm3/(N·m)的低磨损率。

关键词: MoS2/WS2复合薄膜, 盐雾环境, 耐腐蚀性, 摩擦学性能