摘要/Abstract

摘要：

通过在自主研制的热冲压实验线上开展汽车纵梁热冲压实验，探明并对比了无涂层和不同润滑条件下Al-Si涂层22MnB5板对复杂零件热冲压成形质量和组织性能的影响。结果表明：①相比于无涂层板，涂层板能有效改善氧化脱碳现象，但涂层中形成的孔隙和裂纹容易导致零件在成形时产生破裂;采用水基石墨润滑不能消除破裂;采用玻璃润滑能有效避免破裂。②无涂层板的抗拉强度和屈服强度较高，无润滑和石墨润滑涂层板次之，玻璃润滑涂层板的抗拉强度和屈服强度较低;无涂层板的延伸率较涂层板的延伸率大。③玻璃润滑涂层板的表面粗糙度较小，无涂层板次之，无润滑和石墨润滑涂层板的表面粗糙度较大。

关键词: 高强钢, 热冲压, 复杂件, 涂层, 润滑

Abstract:

Experiments on hot stamping of car carlings were performed on independently developed test line, and the effects of uncoated and Al-Si coated sheets of 22MnB5 under various lubrications on forming quality, microstructures and properties of complex parts were revealed and compared. The results obtained show that: ①compared with the uncoated sheet (US), the depths of oxidation and decarburization are reduced by using the coated sheet (CS), but pores and cracks are formed in the coating during forming, which results in fractures in parts. The fractures can not be eliminated under water-based graphite lubrication,and application of glass lubrication can avoid fractures. ②The US is higher in tensile and yield strengths than the CS under no lubrication and water-based graphite lubrication, and the CS under glass lubrication is lowest. The US has a higher elongation than the CS. ③The CS under glass lubrication is lower in surface roughness than the UC, and the CS under no lubrication and water-based graphite lubrication are the highest.

Key words: high strength steel, hot stamping, complex part, coating, lubrication

中图分类号:

TH133.3

王敏, 张春, 张宇, 李少兵, 王琼霜. 汽车高强钢纵梁热冲压实验研究[J]. 中国机械工程, 2016, 27(03): 391-397.

Wang Min, Zhang Chun, Zhang Yu, Li Shaobing, Wang Qiongshuang. Experiments on Hot Stamping of Car Carling of High Strength Steel[J]. China Mechanical Engineering, 2016, 27(03): 391-397.

参考文献

[1]Karbasian H, Tekkaya A E. A Review on Hot Stamping[J]. Journal of Materials Processing Technology, 2010, 210: 2103-2118.

[2]Gui Zhongxiang, Liang Weikang, Zhang Yisheng. Formability of Aluminum-silicon Coated Boron Steel in Hot Stamping Process[J]. Transactions of Nonferrous Metals Society of China, 2014, 24: 1750-1756.

[3]Barcellona A, Palmeri D. Effect of Plastic Hot Deformation on the Hardness and Continuous Cooling Transformations of 22MnB5 Microalloyed Boron Steel[J]. Metallurgical and Materials Transactions A, 2009, 40(5): 1160-1174.

[4]邢忠文, 包军, 杨玉英, 等. 可淬火硼钢板热冲压成形实验研究[J]. 材料科学与工艺, 2008, 16(2): 172-175.

Xing Zhongwen, Bao Jun, Yang Yuying, et al. Hot Stamping Processing Experiments of Quenchable Boron Steel[J]. Materials Science and Technology, 2008, 16(2): 172-175.

[5]姜超, 单忠德, 庄百亮, 等. 热冲压成形22MnB5 钢板的组织和性能[J]. 材料热处理学报, 2012, 33(3): 78-81.

Jiang Chao, Shan Zhongde, Zhuang Bailiang, et al. Microstructure and Properties of Hot Stamping 22MnB5 Steel[J]. Transactions of Materials and Heat Treatment, 2012, 33(3): 78-81.

[6]郭怡晖, 马鸣图, 张宜生, 等. 前防撞梁零件的热成形试制研究[J]. 中国工程科学, 2014, 16(1): 76-80.

Guo Yihui，Ma Mingtu，Zhang Yisheng，et al. Study on the Experiment of Hot Stamping for Front Bumper[J]. Chinese Engineering Science, 2014, 16(1): 76-80.

[7]Gui Zhongxiang, Zhang Yisheng, Li Hongqing, et al. Hot Stamping and Blank Designing for a Vehicle Bumper Using Ultra High Strength Steel[J]. Advanced Materials Research, 2013, 690/693: 2240-2244.

[8]王敏，张春, 肖海峰, 等. 高强钢热冲压中的保压时间效应实验[J]. 塑性工程学报, 2014, 21(2): 88-93.

Wang Min, Zhang Chun, Xiao Haifeng,et al. Experimental Study on Effects of Holding Time on Hot Stamping of High Strength Steel[J]. Journal of Plasticity Engineering, 2014, 21(2): 88-93.

[9]王敏, 张春, 肖海峰, 等. 可淬火硼钢板热成形过程中的传热行为[J]. 锻压技术, 2014, 39(1):29-34.

Wang Min, Zhang Chun, Xiao Haifeng,et al. Heat Transfer Behaviour in Hot Stamping of Quenchable Boron Steel Sheet[J]. Forging & Stamping Technology, 2014, 39(1): 29-34.

[10]Jenner F, Walter M E, Iyengar R M,et al. Evolution of Phases, Microstructure, and Surface Roughness during Heat Treatment of Aluminized Low Carbon Steel[J]. Metallurgical and Materials Transactions A, 2010, 41: 554-1563.

[11]Windmann M, Rttger A, Theisen W. Phase Formation at the Interface between a Boron Alloyed Steel Substrate and an Al-rich Coating[J]. Surface & Coatings Technology, 2013, 226: 130-139.

[12]Jang J H, Lee J H, Joo B D,et al. Flow Characteristics of Aluminum Coated Boron Steel in Hot Press Forming[J]. Transactions of Nonferrous Metals Society of China, 2009, 19: 913-916.

[13]杨洪林, 刘昕, 李俊, 等. 热冲压钢镀层技术的研究现状[J]. 钢铁研究学报, 2013, 25(6): 1-7.

Yang Honglin, Liu Xin, Li Jun, et al.Research Status on Hot Stamping Steel Coating[J]. Journal of Iron and Steel Research, 2013, 25(6): 1-7.

[14]Azushima A, Uda K, Yanagida A. Friction Behavior of Aluminum-coated 22MnB5 in Hot Stamping under Dry and Lubricated Conditions[J]. Journal of Materials Processing Technology, 2012, 212: 1014-1021.

[15]佚名.水基石墨润滑剂试验总结[J]. 固体润滑, 1981(1): 49-53. Anon.Summary of Water-based Graphite Lubricant Experiments[J]. Solid Lubrication, 1981(1): 49-53.

[16]Beuth J L, Klingbeil N W. Cracking of Thin Films Bonded to Elastic-plastic Substrates[J]. Journal of the Mechanics and Physics of Solids, 1996, 44(9): 1411-1428.

[17]Panagopoulos C N, Georgiou E P, Agathocleous P Z, et al. Mechanical Behavior of Zn-Fe Alloy Coated Mild Steel[J]. Materials and Design, 2009, 30: 4267-4272.