半埋藏裂纹金属构件脉冲放电相变应力分析

中国机械工程 ›› 2013, Vol. 24 ›› Issue (21): 2944-2947,2954.

半埋藏裂纹金属构件脉冲放电相变应力分析

付宇明;王俊丽;张帅;郑丽娟

燕山大学,秦皇岛,066004

出版日期:2013-11-10 发布日期:2013-11-15
基金资助:
国家自然科学基金资助项目(51105325, 51075351）
National Natural Science Foundation of China（No. 51105325, 51075351）

Analysis on Phase Change Stress after Pulse Current Discharging of Metal Component with Half-embedding Cracks

Fu Yuming;Wang Junli;Zhang Shuai;Zheng Lijuan

Yanshan University,Qinhuangdao,Hebei,066004

Online:2013-11-10 Published:2013-11-15
Supported by:
National Natural Science Foundation of China（No. 51105325, 51075351）

摘要/Abstract

摘要：

对含半埋藏裂纹的45钢金属构件进行脉冲放电电磁热止裂强化实验,得出脉冲放电电压与止裂强化效果之间的关系，并对止裂强化前后裂尖形貌及显微硬度进行了对比分析，电磁热止裂强化后，裂尖周围显微硬度得到了大幅度的提高;应用Eshelby等效夹杂原理对脉冲放电止裂后裂纹尖端发生组织转变的相变应力进行了理论计算，结果表明，相变应力为压应力,阻止了裂纹的扩展。研究结果为电磁热止裂技术的实际应用奠定了理论基础。

关键词: 电磁热效应, 相变应力, 裂纹, 等效夹杂

Abstract:

The relationship between pulse discharge voltage and arrest-strengthening
effect was analyzed by pulse discharge experiments of 45 steel metal components with half embedding crack.According to the comparisons of the morphology and the micro-hardness near the crack tip before and after the discharge,the micro-hardness near the crack tip after the discharge was improved greatly.The theoretical arithmetic of phase transformation stresses of phase transition region around crack tip after crack arrest strengthening by using the equivalent inclusion principle of Eshelby shows phase transformation stress is compressive stress and it prevents crack propagation,and then a theoretical foundation for the practical applications of electromagnetic thermal arrest techniques is provided.

Key words: electromagnetic heating, phase change stress, crack, equivalent inclusion

中图分类号:

O343.6

付宇明;王俊丽;张帅;郑丽娟. 半埋藏裂纹金属构件脉冲放电相变应力分析[J]. 中国机械工程, 2013, 24(21): 2944-2947,2954.

Fu Yuming;Wang Junli;Zhang Shuai;Zheng Lijuan. Analysis on Phase Change Stress after Pulse Current Discharging of Metal Component with Half-embedding Cracks[J]. China Mechanical Engineering, 2013, 24(21): 2944-2947,2954.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cmemo.org.cn/CN/

https://www.cmemo.org.cn/CN/Y2013/V24/I21/2944

参考文献

[1]Bai Xiangzhong, Fu Yuming, Gao Diankui. Experi- mental Research on Electromagnetic Heating Effects to Stop Crack Propagation in Metal Compo- nents[C]//The 3rd International Conference on Experimental Mechantics. Beijing, 2001 : 257-260.
[2]Fu Yuming, Bai Xiangzhong, Hu Yuda. Technique for Producing Crack Arrest by Electromagnetic Heating[J].Materials Science and Technology, 2001,17 (12) :1653-1656.
[3]Fu Yuming, Tian Zhenguo, Zheng Lijuan. Analysis on the Thermal Stress Field When Cack Arrest in an Axial Symmetry Metal Die Using Electromag- netic Heating[J]. Applied Mathematics and Me- chanics, Z006,8 (3): 53-55.
[4]许峰云[1],徐雪霞[1],白秉哲[1],方鸿生[1].粒状组织的相变残余应力[J].金属学报,2008,44(9):1063-1068.
[5]Lee Chin-- Hyung, Chang Kyong-- Ho. Prediction of Residual Stresses in High Strength Carbon Steel Pipe Weld Conside--ring Solid--state Phase Trans- formation Effects [J].Computers and Structures, 2011,7( 16 ) : 256-265.
[6]徐平光[1],友田[1],阳[1].原位中子衍射材料表征技术的进展[J].金属学报,2006,42(7):681-688.
[7]王平[1,2],白象忠[1].电热止裂相变应力及其对止裂效果的影响[J].中国机械工程,2011,22(8):980-984.
[8]赵严[1],郭鸿镇[1],王涛[1],谭立军[1],姚泽坤[1].等通道转角挤压工艺对TA15合金显微硬度的影响[J].稀有金属材料与工程,2011,40(5):885-888.
[9]Song Hui, Wang ZhongJin. Grain Refinement by Means of Phase Transformation and Recrystalliza- tion Induced by Electropulsing[J].Transactions of Nonferrous Metals Socity of China, 2011,21 ($2) : 353-357.
[10]Eshelby J D. The Determination of the Elastic Field of an Ellipsoidal Inclusion, and Related Problems [J]. Proceeding of the Royal Society of London Se- ries A Mathematical and Sciences, 1957, 241 (1226) :376-396.
[11]付宇明[1],康玮明[1],李伟[1].45钢构件电磁热裂纹止裂后残余应力分析[J].塑性工程学报,2010,17(2):150-153.
[12]Eshelby J D. The Elastic Field Outside an Ellipsoi- dal Inclusion[J]. Proceeding of the Royal Society of London Series A Mathematical and Sciences, 1959, 252(1271) :561-569.

[1]	赵杰, 卢纯, 何家欢, 马亭海, 叶张. 坡道紧急制动工况下货车车轮踏面裂纹扩展行为研究[J]. 中国机械工程, 2025, 36(12): 2811-2819.
[2]	张博, 程明霞, 史云帆, 陈丽. 预变形Jeffcott裂纹转子超谐波共振的动力学响应[J]. 中国机械工程, 2025, 36(11): 2554-2562.
[3]	马天宇, 巩固, 曹宏瑞, 史江海, 尉询楷, 章立军. 8Cr4Mo4V轴承钢微观裂纹萌生与扩展机制的分子动力学模拟[J]. 中国机械工程, 2025, 36(10): 2179-2189.
[4]	李涛, 邓林辉, 莫彬, 石非凡, 刘伟嵬. 基于混合遗传蚁群优化随机森林算法的激光熔覆Ni60裂纹预测与工艺参数优化[J]. 中国机械工程, 2025, 36(06): 1322-1328,1337.
[5]	成艾国1, 王超1, 于万元2, 何智成1. 铆钉裂纹对自冲铆接力学性能影响的仿真与试验研究[J]. 中国机械工程, 2025, 36(02): 197-208.
[6]	孔彦坤1, 邓伟1, 金国忠2, 雷基林1, 陈丽琼3, 贾德文1. 36MnVS4和46MnVS5连杆裂解性能差异性研究及质量缺陷分析[J]. 中国机械工程, 2024, 35(06): 1103-1111，1119.
[7]	张镇, 郭策, 胡财吉, 郑威. 基于增材制造技术的自修复结构设计及修复性能研究[J]. 中国机械工程, 2024, 35(01): 144-151.
[8]	郭伟, 曹宏瑞, 訾艳阳, 尉询楷. 滚动轴承接触疲劳裂纹建模与扩展规律研究[J]. 中国机械工程, 2023, 34(16): 1891-1899.
[9]	朱玉龙, 赵迎松, 方阳, 陈洪恩, 陈振茂, . 孔边裂纹的旋转涡流检测[J]. 中国机械工程, 2023, 34(08): 883-891.
[10]	邢海燕, 朱孔阳, 张钋, 刘传, 段成凯, 刘伟男, 刘超. 裂纹闭合临界状态磁特性表征模型[J]. 中国机械工程, 2023, 34(04): 414-420.
[11]	张帅, 陈照强, 肖光春, 衣明东, 张静婕, 周婷婷, 许崇海. Si3N4/TiC/ZrSi2陶瓷刀具裂纹愈合性能研究[J]. 中国机械工程, 2022, 33(19): 2288-2297.
[12]	孟宗, 李佳松, 潘作舟, 庞修身, 崔玲丽, 樊凤杰. 裂纹故障对轮齿时变啮合刚度的影响分析[J]. 中国机械工程, 2022, 33(16): 1897-1905，1911.
[13]	董龙龙, 俞树荣, 李淑欣, 宋伟. 滚动接触下裂纹充液行为研究[J]. 中国机械工程, 2022, 33(10): 1210-1218.
[14]	闫梁, 万本例, 胡斌, 范孟豹. 不锈钢表面裂纹方向电磁检测方法[J]. 中国机械工程, 2022, 33(09): 1057-1064.
[15]	周海, 张杰群, 徐亚萌, 沈军州, 黄梦蝶. 单颗磨粒刻划氧化镓晶体表面的裂纹成核位置及扩展方向研究[J]. 中国机械工程, 2021, 32(16): 1945-1951.