China Mechanical Engineering ›› 2011, Vol. 22 ›› Issue (20): 2494-2497.

Previous Articles     Next Articles

Anti-erosion Analysis for Artillery Barrel Coated by Electrical Explosion Spraying Technology

Jiang Xiaolin1;Wang Yanni2,3;Lu Xin4
  

  1. 1.China North Industries Planning Institute,Beijing,100053
    2.Beijing Union University,Beijing,100101
    3.Beijing Institute of Technology,Beijing,100081
    4.Beijing Research Institute of Mechanical & Electrical Technology,Beijing,100831
  • Online:2011-10-25 Published:2011-11-02

电爆炸喷涂技术用于提高炮管的抗烧蚀性分析

蒋啸林1;王燕妮2,3;陆辛4   

  1. 1.中国兵器工业规划研究院,北京,100053
    2.北京联合大学,北京,100101
    3.北京理工大学,北京,100081
    4.北京机电研究所,北京,100831

PDF

Abstract:

Researches on the mechanism of improving anti-erosion in artillery barrel were done in order to enhance anti-erosion property of artillery barrel. Coating prepared by electrical explosion spraying technology was compared in performance with chrome plating. The experimental results show that coating prepared by electrical explosion spraying technology is significantly better in anti-erosion performance than coating prepared by chrome coating. Electrical explosion spraying technology is an effective method to prepare high quality coating for research of anti-erosion property of artillery barrel.

Key words: artillery barrel, chrome coating, anti-erosion, electrical explosion spraying

摘要：

为进一步提高火炮身管内膛的抗烧蚀性能,对火炮身管内膛表面改性涂层应具备的特性进行了分析，利用电爆炸喷涂技术制备了涂层,并将其与电镀铬镀层进行了性能对比试验。试验结果表明，利用电爆炸喷涂技术可制备出抗烧蚀性能显著优于镀铬层的涂层。在今后延长火炮身管抗烧蚀寿命研究过程中，运用电爆炸喷涂技术是制备高品质涂层的一种有效方法。