Effects of Different Arc Rates on Interface Behavior of Ni201 Repaired Layers by Electro-spark Deposition

Abstract

Abstract: The key factor affected on the quality of the repaired layers was determined by the processing parameter selection of remanufacturing equipment. Ni201 repaired layers on Q235 steel surface were prepared by electro-spark deposition technology, the effects of different arc rates on the quality repaired layers were analyzed. The microstructure, chemical elements distribution and phase composition of the bonding interface between repaired layer and substrate were investigated by means of scanning electron microscopy and energy dispersive spectrometer, and X-ray diffraction. The results show that the value of arc rate is between 35%～45%, the microstructure of the repaired layers is uniform and dense, the interdiffusion of elements demonstrates that the repaired layer is bonded metallurgically with the base, the main phase of the layer is composed of Fe19Ni， Co3Fe7， Fe0.9Si0.1 and C0.055Fe1.945 .

Key words: electro-spark deposition, arc rate, Q235 steel, interface behavior

摘要： 再制造修复设备工艺参数选择是决定修复层质量的关键因素。利用电火花沉积技术，在Q235钢表面制备Ni201修复改性层，对比分析弧比取不同值时对修复层质量的影响，并利用扫描电镜(SEM)、能谱仪(EDS)、X射线衍射(XRD)等检测方法，研究了修复层与基体结合界面的微观结构、元素分布及相组成。结果表明：弧比取值在35%～45%之间时，修复层组织均匀致密，基体元素与修复层元素相互扩散形成冶金结合，修复层主要由Fe19Ni、Co3Fe7、Fe0.9Si0.1和C0.055Fe1.945相组成。

关键词: 电火花沉积, 弧比, Q235钢, 界面行为

CLC Number:

TG174.44

Zhao Yuncai, Liu Zongyang, Yang Leilei. Effects of Different Arc Rates on Interface Behavior of Ni201 Repaired Layers by Electro-spark Deposition[J]. China Mechanical Engineering.

赵运才, 刘宗阳, 杨雷雷. 弧比变化对电火花沉积Ni201修复层界面行为的影响[J]. 中国机械工程.

References

[1]李占明,朱有利,孙晓峰，等.电火花沉积技术的研究与应用进展[J].热加工工艺,2013,42(24):32-36.

Li Zhanming, Zhu Youli, Sun Xiaofeng, et al.Development in Research and Application of Electro-spark Deposition Technology[J]. Hot Working Technology,2013,42(24):32-36.

[2]孙凯伟,张琪娜,涂益民，等.电火花沉积技术国内外研究的最新进展[J].焊接技术,2014,43(8):1-5.

Sun Kaiwei, Zhang Qina, Tu Yimin, et al. The Recent Research Status of the Electro Spark Deposition[J]. Welding Technology, 2014,43(8):1-5.

[3]沈晔超,宋守许,王玉琳,等.基于汽车驱动桥壳再制造的堆焊可靠性研究[J].中国机械工程,2013,24(5):676-680.

Shen Yechao, Song Shouxu, Wang Yulin, et al. Reliability of Welded Surfacing Layer for Remanufacture of Vehicles Drive Axle Housing[J]. China Mechanical Engineering,2013,24(5):676-680.

[4]田亮,刘振英,罗宇,等.面向再制造的硬面堆焊技术研究现状和展望[J].电焊机,2015,45(2):11-18.

Tian Liang, Liu Zhenying, Luo Yu, et al. Status and Development Prospects of Hardfacing Technology for Remanufacturing[J]. Electric Welding Machine,2015,45(2):11-18.

[5]徐滨士,马世宁,刘世参,等.21世纪的再制造工程[J].中国机械工程,2000,11(1/2):36-39.

Xu Binshi, Ma Shining, Liu Shican, et al. Remanufacturing Engineering in 21st Century[J]. China Mechanical Engineering,2000,11(1/2):36-39.

[6]陈龙,孟惠民,黄亮亮,等.45钢表面电火花沉积多层YG8涂层的组织和耐磨性[J].材料热处理学报,2013, 34(11):170-175.

Chen Long, Meng Huimin, Huang Liangliang, et al. Microstructure and Wear Property of Multi-layer YG8 ESD Coating on 45 Steel[J]. Transactions of Materials and Heat Treatment,2013,34(11):170-175.

[7]孙凯伟,于华,吴公一,等.TA2表面电火花沉积NiCr涂层的界面行为[J].焊接技术,2015,44(4):10-12.

Sun Kaiwei, Yu Hua, Wu Gongyi, et al. Interface Behavior of NiCr Coating on TA2 Produced by Electrospark Deposition[J]. Welding Technology,2015,44(4):10-12.

[8]王建升,王华昆,钟毅,等.H13钢电火花沉积层组织结构的研究[J].中国表面工程,2003,16(6):27-30.

Wang Jiansheng, Wang Huakun, Zhong Yi, et al. Microstructure of Electron-spark Deposited Coating on H13 Steel[J]. China Surface Engineering,2003,16(6):27-30.

[9]Yu Hua, Shi Hongxin, Wang Yaoli, et al. NiCr Alloy Coating Deposited on the Surface of 35CrMo Steel by the Electro Spark Process[J]. Materials Science Forum,2008,575-578:827-832.

[10]Ebrahimnia M, Malek Ghaini F, Xie Y J, et al. Microstructural Characteristics of the Built Up Layer of a Precipitation Hardened Nickel Based Superalloy by Electrospark Deposition[J]. Surface and Coatings Technology,2014,258:515-523.

[11]王燕,张富巨.Q235钢电火花堆焊接头行为研究[J].电焊机,2014,44(3):122-125.

Wang Yan, Zhang Fuju. Research on the Joint Behavior of Electro-spark Deposition on Q235 Steel[J]. Electric Welding Machine, 2014, 44(3): 122-125.