Prediction of Residual Life of Pre-corrosion Aluminum Alloy with Fractal Dimension

China Mechanical Engineering ›› 2013, Vol. 24 ›› Issue (17): 2337-2340.

Previous Articles Next Articles

Prediction of Residual Life of Pre-corrosion Aluminum Alloy with Fractal Dimension

Zhang Chuan1;Yao Weixing2

1.Key Laboratory of Fundamental Science for National Defense-advanced Design Technology of Flight Vehicle,Nanjing University of Aeronautics and Astronautics,Nanjing,210016
2.State Key Laboratory of Mechanics and Control of Mechanical Structures,
Nanjing University of Aeronautics and Astronautics,Nanjing,210016

Online:2013-09-10 Published:2013-09-22

铝合金预腐蚀剩余寿命的分形维数预测方法

张川1;姚卫星2

1.南京航空航天大学飞行器先进设计技术国防重点学科实验室,南京,210016
2.南京航空航天大学机械结构力学及控制国家重点实验室,南京,210016

基金资助:
江苏省“青蓝工程”科技创新团队资助项目(1001-YPB11001)；江苏高校优势学科建设工程资助项目

Abstract

Abstract:

Several smooth specimens of aluminum alloy LC4CS soaked in EXCO solution for different time were measured to obtain corrosion surface profiles and then tested to obtain residual life. The relationship between pre-corrosion residual life and fractal dimension of profile near fracture for different pre-corrosion time were discussed. Fractal dimension was selected as pre-corrosion damage parameter on residual life. The results show that fractal dimension of corrosion surface profile near fracture is influenced little by dispersion of corrosion surface, and there is a linear relationship between fractal dimension and residual life, which is not related with loading. The residual lives calculated by fractal dimensions are in twice scatter band.

Key words: pre-corrosion, damage parameter, fractal dimension, residual life

摘要：

试验得到在EXCO溶液中预腐蚀不同时间的LC4CS光滑试件的腐蚀表面轮廓线和剩余疲劳寿命。分析了预腐蚀剩余寿命和断口附近轮廓线分形维数随预腐蚀时间的变化规律,针对该规律选取分形维数为预腐蚀剩余寿命损伤参量。试验结果表明：断口附近腐蚀表面轮廓线的分形维数受腐蚀形貌分散性的影响较小,与剩余寿命呈线性关系且与载荷无关,由分形维数计算得到的剩余寿命处于二倍分散带之内。

关键词: 预腐蚀, 损伤参量, 分形维数, 剩余寿命

CLC Number:

Zhang Chuan1;Yao Weixing2. Prediction of Residual Life of Pre-corrosion Aluminum Alloy with Fractal Dimension[J]. China Mechanical Engineering, 2013, 24(17): 2337-2340.

张川1;姚卫星2. 铝合金预腐蚀剩余寿命的分形维数预测方法[J]. 中国机械工程, 2013, 24(17): 2337-2340.

[1]	Zhang Xueliang, Wang Yusong, Wen Shuhua, Fan Shirong, Chen Yonghui, Lan Guosheng. Logarithmic Wavelet Spectrum Method for Computing Fractal Dimension of Machined Surface Profiles [J]. China Mechanical Engineering, 2016, 27(23): 3142-3148.
[2]	Hui Li, Yu Xiang, Xu Liang, Zhou Song, Wang Lei. On Quantitative Techniques of Corrosion Pits of Aerial Aluminum Alloys [J]. China Mechanical Engineering, 2015, 26(16): 2233-2236,2243.
[3]	Li Gang, Yang Qinghua, Wen Donghui, Lu Congda. Effects of Diamond Abrasive Arraying Forms on Interdigitated Micro-channel [J]. China Mechanical Engineering, 2015, 26(10): 1374-1380.
[4]	He Qun;Li Lei;Jiang Guoqian;Xie Ping. Residual Life Predictions for Bearings Based on PCA and MELM [J]. China Mechanical Engineering, 2014, 25(7): 984-989.
[5]	Zhang Huailiang;Zou Baiwen;Xiao Lei. A Novel Identification Algorithm for Fractal Scaling Regionof Wear Particles [J]. China Mechanical Engineering, 2014, 25(3): 371-376.
[6]	LI Chao, JIAO Yu, ZHANG Jing, DIAO Man. Research on Correlation of Friction Signals and Surface Topography of PEEK [J]. China Mechanical Engineering, 2011, 22(14): 1715-1719.
[7]	JU Wen-Dong, HUANG Chang-Hui, OU Yang-Xiao-Qin, ZHENG Qiang. White Light Phase-shifting Interferometer Detection, Reconstruction and Fractal Characterization of Alloy Dimple Fracture 3D Microstructure [J]. China Mechanical Engineering, 2010, 21(22): 2675-2678.

Prediction of Residual Life of Pre-corrosion Aluminum Alloy with Fractal Dimension

铝合金预腐蚀剩余寿命的分形维数预测方法

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 7

Recommended Articles

Metrics