22MnB5热变形行为研究及本构方程建立

摘要/Abstract

摘要：

以22MnB5为实验材料,在500~950℃范围内和应变速率为0.01s-1、0.1s-1、1s-1的实验条件下,采用热模拟机Gleeble-1500对硼钢进行热拉伸实验,研究了不同变形条件下硼钢的热流变行为;对拉断后的试样断面进行组织分析,阐述了不同变形条件下硼钢的组织对热流变行为变化的影响。研究表明：硼钢的热变形行为属于典型的动态回复型,其流动应力随着温度的升高而减小,随着应变速率的增大而增大,且温度对流动应力的影响更显著;在500℃、应变速率0.01s-1的条件下,硼钢高温下的热力学行为与上述规律有所差别,其流变应力高于高应变速率下的流变应力。最后根据高温拉伸实验所得数据,构建了22MnB5热变形的本构方程,以此来描述硼钢高温下的热流变行为。

关键词: 硼钢, 热变形行为, 显微组织, 本构模型

Abstract:

Hot tensile tests of 22MnB5 were carried out with Gleeble-1500 at the temperatures varying from 500℃ to 950℃ and at the strain rates of 0.01s-1, 0.1s-1, 1s-1 to study its hot deformation behavior at high temperature. Afterwards, microstructure analysis of the cross sections of specimens was conducted to clarify the relationship between microstructure and hot deformation of boron steel under different conditions. The results show that the mechanism of hot deformation of 22MnB5 belongs to dynamic recovery and that the flow stress decreases with the increase of temperature and with the reduction of strain rate. In addition, the influence of temperature is more obvious than it of strain rate. However, the flow stress at the temperature of 500℃ and at the strain rate of 0.01s-1 is higher and the result seems a little different to the above law. Finally, constitutive model was established to represent the behavior of hot deformation of boron steel at high temperature.

Key words: boron steel, hot deformation behavior, microstructure, constitutive model

中图分类号:

TG306

曹淑芬, 张立强, 郭鹏程, 李落星. 22MnB5热变形行为研究及本构方程建立[J]. 中国机械工程, 2014, 25(9): 1256-1261.

Cao Shufen, Zhang Liqiang, Guo Pengcheng, Li Luoxing. Study on Hot Deformation Behavior and Flow Stress Constitutive Model of 22MnB5 at High Temperature[J]. China Mechanical Engineering, 2014, 25(9): 1256-1261.

参考文献

[1]王利, 杨雄飞, 陆匠心. 汽车轻量化用高强度钢板的发展[J]. 钢铁, 2006, 41(9): 1-8.
Wang Li, Yang Xiongfei, Lu Jiangxin.Development of High Strength Steel Sheets for Lightweight Automobile[J]. Iron and Steel, 2006, 41(9): 1-8.
[2]李辉平,赵国群,贺连芳,等. 热冲压硼钢B1500HS高温本构方程的研究[J]. 机械工程学报, 2012, 48(8):21-22.
Li Huiping, Zhao Guoqun, He Lianfang, et al. Research on the Constitutive Relationship of Hot Stamping Boron Steel B1500HS at High Temperature[J]. Journal of Mechanical Engineering, 2012, 48(8):21-22.
[3]胡琦. 超高强度硼钢板热冲压的力学性能研究[D]. 上海: 同济大学, 2008.
[4]刘俊. 温度-组织-应力耦合关系及在焊接中的应用[D].上海:上海交通大学, 2009.
[5]Naderi M. Hot Stamping of Ultra High Strength Steels[D].Iran: Universittsbibliothek, 2007.
[6]Karbasian H, Tekkaya A E.A Review on Hot Stamping[J]. Journal of Materials Processing Technology, 2010, 210(15): 2103-2118.
[7]唐志勇,江海涛,唐荻,等. 热冲压成形27MnCrB5钢组织与力学性能研究[C]//中国钢铁年会论文集. 北京:冶金工业出版社, 2007：5-75.
[8]Merklein M, Lechler J. Investigation of the Thermo-mechanical Properties of Hot Stamping Steels[J]. Journal of Materials Processing Technology, 2006, 177:452-455.
[9]Naderi M, Durrenberger L, Molinari A, et al. Constitutive Relationships for 22MnB5 Boron Steel Deformed Isothermally at High Temperatures[J].Materials Science and Engineering A, 2008, 478:130-139.
[10]庄百亮,单忠德,姜超,等. 汽车防撞梁高强钢热成形工艺研究[J].中国机械工程, 2012, 23(2):225-228.
Zhuang Bailiang, Shan Zhongde, Jiang Chao, et al. Research on Ultra-high-strength-steel Hot Stamping Process of Automotive Anti-collision Beam[J]. Chinese Mechanical Engineering, 2012, 23(2):225-228.
[11]周记明，齐乐华，陈国定. 热成形中金属本构关系建模方法综述[J].机械科学与技术, 2005, 24(2):212-213.
Zhou Jiming, Qi Lehua, Chen Guoding.Investigation on the Constitutive Relationship of Material Forming in High Temperature[J]. Mechanial Science and Technology, 2005, 24(2):212-213.
[12]Sellars C M,Mctegart W J. On the Mechanism of Hot Deformation[J]. Acta Metall, 1966, 14:l136-1138.

[1]	汪宏辉, 董淑磊, 钱建康, 汤克刚, 王志航, 秦熙琨, 雷正龙. 预热及保温对严寒环境X80钢管道全自动外焊焊缝组织与性能的影响[J]. 中国机械工程, 2021, 32(06): 748-755.
[2]	刘志强, 赵杰, 王克环, 武永, 吕良星, 刘钢, 苑世剑, . [成形过程仿真优化与集成计算材料工程]钛合金热成形工艺形变与组织演变耦合多尺度仿真研究进展[J]. 中国机械工程, 2020, 31(22): 2678-2690,2698.
[3]	孙宇飞1;赵长财1;杨盛福2;杨卓云1. AA7075板材热处理的增塑机制及成形性能[J]. 中国机械工程, 2020, 31(17): 2128-2136.
[4]	聂昕1;肖兵兵1;申丹凤2;郭文峰1. 考虑变形热和摩擦热效应的热力耦合冲压研究[J]. 中国机械工程, 2020, 31(16): 2005-2015.
[5]	陈明和;王宁. 高强铝合金热塑性变形本构关系研究现状及发展趋势[J]. 中国机械工程, 2020, 31(08): 997-1007.
[6]	付宇明, 赵华洋, 郑丽娟, 齐童. 多元陶瓷相在激光熔覆层中的溶解机制研究[J]. 中国机械工程, 2019, 30(23): 2884-2889,2897.
[7]	林建斌;吕涛;黄水泉;胡晓冬;许雪峰. 基于静电微量润滑技术的磨削加工性能试验研究[J]. 中国机械工程, 2018, 29(23): 2783-2791,2798.
[8]	张宏建1;温卫东1,2;崔海涛1;肖健峰1. IC10合金的动态回复/再结晶本构行为研究[J]. 中国机械工程, 2017, 28(18): 2256-2261.
[9]	艾建光, 姜峰, 言兰. TC4-DT钛合金材料动态力学性能及其本构模型[J]. 中国机械工程, 2017, 28(05): 607-616.
[10]	王力锋, 刘凤德, 刘双宇, 张宏, 刘薇娜, 田淼磊, . 高氮钢复合焊接接头组织与力学性能研究[J]. 中国机械工程, 2016, 27(24): 3382-3388.
[11]	申卫国, 方艳, 董玲, 岑虎, 王春娴, 顾振杰. 液压支架激光熔覆不锈钢合金涂层的实验研究[J]. 中国机械工程, 2015, 26(18): 2533-2538.
[12]	王巧玲, 唐炳涛, 郑伟. 一种修正的Norton-Hoff本构模型及实验验证[J]. 中国机械工程, 2015, 26(14): 1978-1982.
[13]	付宇明, 刘明, 郭建龙, 郑丽娟. 脉冲磁处理金刚石结块的实验及磁场数值模拟[J]. 中国机械工程, 2015, 26(14): 1983-1986.
[14]	王蔚1,2;刘永贤1;Fuh Y. X. Jerry3. ZrO2对激光烧结Al2O3/SiO2/ZrO2显微组织和显微硬度的影响[J]. 中国机械工程, 2014, 25(6): 727-731.
[15]	丁兰英1，2;苏宏华1;徐鸿钧1;丁文锋1;范敏1. 有机粘结固体润滑剂涂层砂轮磨削性能研究[J]. 中国机械工程, 2013, 24(21): 2927-2932.