热成形钢板与双相钢板焊点失效模式研究

摘要/Abstract

摘要： 针对热成形钢板与双相钢板的焊点失效模式，采用试验+模拟的方法进行研究。通过数值模拟得到了合适的焊接工艺窗口，在此基础上研究了焊接时间、熔核偏移等对焊点力学性能的影响。拉剪试验结果表明：随着焊接时间的延长，焊点失效模式由界面断裂向熔核拔出转变。研究失效模式发现，熔核偏移对熔核拔出失效部位影响极大，即薄板与厚板焊接时，熔核更容易从薄板拔出；板厚相同时，熔核更容易从热成形钢侧拔出。最后结合试验数据建立了焊点力学模型，得到热成形钢板和双相钢板焊点失效准则。

关键词: 焊接时间, 拉剪强度, 硬度分布, 焊点失效准则

Abstract: The failure mode of welding spots between hot-formed steel sheet and dual-phase steel sheet was studied by tests and numerical simulations, finite element(FE) model was built to simulate the resistance spot welding(RSW) process. So as the welding lobe got, the effects of welding time and positive deviation of fusion zone(FZ) on mechanics properties of welding spots were researched. As the tensile-shear test shown, with the increase of welding time, the failure mode of welding spots transited from interface fracture(IF) to pullout failure(PF) . At the same time, it is found that the positive deviation of FZ has a great influence on starting positions of PF. when the thin sheet welded with thick sheet, the welding spots were easier to be pulled out from the thin sheet sides, when the sheet thickness is the same, the welding spots were easier to be pulled out from the hot-formed steel sides. Finally, the welding spot mechanics model was established based on experimental data, the welding spot failure criteria was obtained.

Key words: welding time, tensile-shear strength, hardness distribution, welding spot failure criteria

中图分类号:

TG453.9

聂昕;陈焕焕. 热成形钢板与双相钢板焊点失效模式研究[J]. 中国机械工程.

NIE Xin;CHEN Huanhuan. Research on Failure Mode of Welding Spots between Hot-formed Steel Sheet and Dual-phase Steel Sheet[J]. China Mechanical Engineering.

参考文献

[1]林建平,胡琦,王立影,等.USIBOR1500超高强度淬火钢板点焊性能研究[J].中国工程机械学报，2007,5(3): 317-321.
LIN Jianpin, HU Qi, WANG Liying, et al. Spot Welding Property Study of Ultra High Strength Quenching Steel Plate USIBOR1500[J].Chinese Journal of Construction Machinery， 2007,5(3):317-321.
[2]陈飞,李敬勇.车用热成形钢板 USIBOR1500P+电阻点焊焊接工艺优化及接头组织与性能[J].热加工工艺，2016,45(7):51-54.
CHEN Fei, LI Jingyong. Resistance Spot Welding Process Optimization and Microstructure and Performance of Joint of USIBOR1500P+ Hot Forming Steel Sheet[J].Hot Working Technology， 2016,45(7): 51-54.
[3]IGHODARO O L, BIRO E, ZHOU Y N. Comparative Effects of Al-Si and Galvannealed Coatings on the Properties of Resistance Spot Welded Hot Stamping Steel Joints[J]. Journal of Materials Processing Technology， 2016, 236:64-72.
[4]LIU Chengjie, ZHENG Xiankun, HE Hongyu, et al. Effect of Work Hardening on Mechanical Behavior of Resistance Spot Welding Joint during Tension Shear Test[J].Materials and Design， 2016,100:188-197.
[5]郑文,王敏,孔谅,等.超高强度热成形钢电阻点焊的数值模拟[J].上海交通大学学报，2012,46(7):1074-1078.
ZHEN Wen, WANG Min, KONG Liang, et al. Numerical Simulation in Resistance Spot Welding of Ultra High Strength Hot Formed Steel[J]. Journal of Shanghai Jiaotong University, 2012,46(7):1074-1078.
[6]宇慧平,王伟伟.超高强钢点焊结构的基础力学性能研究[D].北京：北京工业大学，2012.
YU Huiping, WANG Weiwei. Basic Mechanical Properties Analysis of Ultra High Strength Steel Welding Structure[D]. Beijing: Beijing University of Technology, 2012.
[7]LIANG Xuebo, YUAN Xinjian, WANG Haodong, et al. Microstructure, Mechanical Properties and Failure Mechanisms of Resistance Spot Welding Joints between Ultra High Strength Steel B1500HS and Galvanized Steel HSLA350[J]. International Journal of Precison Engineer and Manufacturing, 2016,17(12):1659-1664.
[8]THIBAUT H, SYLVAIN D. Investigation of the Failure of Advanced High Strength Steels Heterogeneous Spot Welds[J]. Metals, 2016,6(111):321-322.
[9]杜汉斌,刘成杰,王武荣,等.热成形B1500HS硼钢与DP780双相钢点焊焊接性及仿真分析[J].上海金属,2017,39(1):20-26.
DU Hanbin, LIU Chengjie, WANG Wurong, et al. Weldability and Numerical Study of the Resistance Spot Weld of Hot-formed B1500HS Boron Steel and DP780 Dual-phase Steel[J].Shanghai Metals, 2017,39(1):20-26.
[10]余海燕,孙喆.超高强度钢与镀锌双相钢电阻点焊接头强度试验[J].焊接技术,2011,40(11):6-9.
YU Haiyan, SUN Zhe. Experimental Study on Strength of Resistance Spot Welded Joint of Ultra High Strength Steel and Galvanized Dual Phase Steel[J].Welding Technology, 2011,40(11):6-9.
[11]谷铮巍,张正林,李欣,等.超高强度钢与微合金钢点焊接头的组织与性能[J].吉林大学学报,2009,39 (3):624-626.
GU Zhengwei, ZHANG Zhenglin, LI Xin, et al. Microstructure and Property of Spot Welded Joint of Ultra High Strength Steel and Micro-alloy Steel[J]. Journal of Jilin University, 2009, 39(3): 624-626.
[12]General Motors. Automotive Welding Handbook[M]. Detroit: General Motors, 1996.
[13]SALVINI P, VULLO V, VIVIO F, et al. One Shot Failure Modes in Spot Welded Structures[J]. Welding International, 2005,19(4):297-304.
[14]张小云.双相钢点焊熔核界面撕裂失效机理与控制方法研究[D].上海：上海交通大学，2008.
ZHANG Xiaoyun. Research on Weld Nugget Interface Tearing Failure Mechanism and Control Methods of Dual Phase Steel[D].Shanghai：Shanghai Jiaotong University, 2008.
[15]ZHAO Dawei, WANG Yuanxun, LIANG Dongjie, et al. Modeling and Process Analysis of Resistance Spot Welded DP600 Joints Based on Regression Analysis[J]. Materials and Design，2016,110:676-684.
[16]陈树君，郝素锋.热冲压高强钢点焊接头失效行为研究[D].北京：北京工业大学，2013.
CHEN Shujun,HAO Sufeng.Study on Failure Behavior of Hot Stamping High Strength Steel Spot Welds[D].Beijing：Beijing University of Technology，2013.