Formability of AZ31 Magnesium Alloy Sheet under Warm and Electromagnetic Forming Condition

Meng Zhenghua1，2;Huang Shangyu2;Hu Jianhua2;Hu Tingting2

1.Hubei Key Laboratory of Advanced Technology of Automotive Parts,Wuhan,430070

2.Wuhan University of Technology,Wuhan,430070

Online:2011-01-25 Published:2011-01-27
Supported by:

National Natural Science Foundation of China（No. 50875192）;
Fundamental Research Funds for the Central Universities

摘要/Abstract

摘要：

将电磁成形和温热成形方法相结合，以AZ31镁合金板材为对象，测试了25℃至230℃内AZ31镁合金板材的极限应变，得到了AZ31镁合金板材在温热电磁成形条件下的成形极限图。温热电磁成形条件下的成形与准静态胀形结果对比表明：随温度提高，镁合金板材温热电磁成形的极限得到提高;相比于单一电磁成形和单一温成形，温热电磁成形可获得更大的极限变形，从而有利于提高材料的成形能力。

关键词:

镁合金, 成形能力, 电磁成形, 成形极限图

Abstract:

EMF and warm forming were combined to improve the formability of Mg alloy sheets herein.The limit strains of AZ31 magnesium sheet using warm and electromagnetic forming (WEMF) at different temperatures (25-230℃) were obtained. The forming limit diagrams (FLD) of AZ31 magnesium sheet under WEMF conditions were established to contrast with FLDs of traditional warm forming. The results show that: the forming limit of AZ31 sheet of WEMF increases with the temperature; in comparison with EMF and warm forming respectively, WEMF improves the formability of Mg alloy sheets. 

Key words:

magnesium alloy, formability, electromagnetic forming(EMF), forming limit diagram

中图分类号:

TG391]

孟正华, 黄尚宇, 胡建华, 胡婷婷.

AZ31镁合金板材温热电磁成形能力

[J]. 中国机械工程, 2011, 22(2): 239-242.

MENG Zheng-Hua, HUANG Chang-Yu, HU Jian-Hua, HU Ting-Ting.

Formability of AZ31 Magnesium Alloy Sheet under Warm and Electromagnetic Forming Condition

[J]. China Mechanical Engineering, 2011, 22(2): 239-242.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://www.cmemo.org.cn/CN/

http://www.cmemo.org.cn/CN/Y2011/V22/I2/239

参考文献

[1]Friedrich H,Schumann S. Research for a "New Age of Magnesium" in the Automotive Industry[J]. Journal of Materials Processing Technology, 2001, 117(3) :276-281.
[2]冯美斌[1].汽车轻量化技术中新材料的发展及应用[J].汽车工程,2006,28(3):213-220.
[3]Kojima Y. Platform Seienee and Teehnology for Advanced Magnesium Alloys[J]. Materials Science Forum, 2000,350/351 : 3-18.
[4]张士宏[1],王忠堂[2],周丽新[1],徐永超[1].镁合金板件温热成形技术的几个新进展[J].材料导报,2006,20(8):114-118.
[5]Iwanaga K, Tashiro H, Okamoto H, et al. Improvement of Formability from Room Temperature to Warm Temperature in AZ31 Magnesium Alloy[J]. Journal of Materials Processing Technology, 2004, 155/156 : 1313-1316.
[6]Doege E, Droder K. Sheet Metal Forming of Magnesium Wrought Alloys- formability and Process Technology [J].Journal of Materials Processing Technology, 2001,115 (1) : 14-19.
[7]Yoshihara S, Manabe K, Nishimura H. Effect of Blank Holder Force Control in Deep- drawing Process of Magnesium Alloy Sheet[J]. Journal of Materials Processing Technology, 2005, 170 ( 3 ) : 579-585.
[8]Yoshihara S, Yamamoto H, Manabe K. Formability Enhancement in Magnesium Alloy Deep Drawing by Local Heating and Cooling Technique[J]. Journal of Materials Processing Technology, 2003, 143/144: 612-615.
[9]Zhang S H,Zhang K,Xu Y C,et al. Deep--drawing of Magnesium Alloy Sheets at Warm Temperatures [J]. Journal of Materials Processing Technology, 2007,185 (1/3) : 147-151.
[10]苌群峰[1],李大永[1],彭颖红[1],曾小勤[2].AZ31镁合金板材温热冲压数值模拟与实验研究[J].中国有色金属学报,2006,16(4):580-585.
[11]Chen F K, Huang T B. Formability of Stamping Magnesium- alloy AZ31 Sheets [J]. Journal of Materials Processing Technology, 2003, 142 (3) : 643-647.
[12]Sheng Z Q, Shivpuri R. A Hybrid Process for Forming Thin--walled Magnesium Parts[J]. Materials Science and Engineering A, 2006, 428(1/2) .. 180-187.
[13]于彦东[1,2],李彩霞[1].镁合金AZ31B板材热拉深成形工艺参数优化[J].中国有色金属学报,2006,16(5):786-792.
[14]张星[1],张治民[1],李保成[1].AZ31镁合金动态力学行为实验研究[J].弹箭与制导学报,2007,27(4):226-227.
[15]孟正华[1],黄尚宇[1].高速率成形中材料成形性的影响因素[J].锻压技术,2007,32(4):1-6.
[16]李春峰[1],于海平[1].电磁成形技术理论研究进展[J].塑性工程学报,2005,12(5):1-7.
[17]Mamalis A G,Manolakos D E,Kladas A G,et al. Electromagnetic Forming and Powder Processing: Trends and Developments[J]. Appl. Mech. Rev. , 2004,57(4):299-324.
[18]Kamal M. A Uniform Pressure Electromagnetic Actuator for Forming Flat Sheets[D]. Columbus: The Ohio State University,2005.
[19]Meng Zhenghua, Huang Shangyu, Yang Mei. Effects of Processing Parameters on Density and Electric Properties of Electric Ceramic Compacted by Low Voltage Electromagnetic Compaction[J].Journal of Materials Processing Technology,2009, 209(2) :672-678.
[20]陈振华.变形镁合金[M].北京:化学工业出版社,2005.185-186.