DD5缓进磨削表面粗糙度和硬化率对疲劳性能影响研究

doi:10.3969/j.issn.1004-132X.2024.08.015

摘要/Abstract

摘要： 为研究DD5镍基单晶高温合金缓进磨削表面粗糙度和硬化率对疲劳性能的影响规律及机理，设计实验并进行了试件磨削与疲劳性能测试。结果表明：表面粗糙度的增大引起应力集中加剧,导致疲劳性能降低，不同磨削工艺下表面粗糙度由0.347 μm增大到0.687 μm，其疲劳寿命由5.51×105降至3.38×105，下降率约38.66%；表面粗糙度小于0.4 μm时表面硬化可提高试件疲劳寿命，表面粗糙度超过0.4 μm时表面硬化对疲劳性能的影响不显著；形貌测试结果表明，随着表面粗糙度的提高，磨削表面耕犁产生的沟壑数量和深度均增大，疲劳载荷作用下磨削表面裂纹源数量增加、应力集中加剧，从而导致疲劳寿命降低。较小的表面粗糙度与较大的表面硬化率均可提高DD5缓进磨削疲劳性能。

关键词: DD5高温合金, 缓进磨削, 表面粗糙度, 表面硬化率, 疲劳性能, 断裂机理

Abstract: In order to study the influence laws and mechanism of surface roughness and hardening rate on fatigue property of DD5 nickel-based single crystal superalloy during creep feed grinding, the experiments were designed and tested. The results show that the increase of surface roughness leads to the aggravation of stress concentration and decrease of fatigue property. Under different grinding processes, when the value of surface roughness increases from 0.347 μm to 0.687 μm, the fatigue life decreases from 5.51×105 to 3.38×105, and the reduction rate is about 38.66%. When the value of surface roughness is less than 0.4 μm, the surface hardening may improve the fatigue life of the specimen. When the value of surface roughness is more than 0.4 μm, the surface hardening has no significant effect on the fatigue property. The morphological tests show that with the increase of surface roughness, the number and depth of gullies generated by ploughing on the grinding surface increase, the number of crack sources on the grinding surface increases and the stress concentration intensifies under fatigue load, which leads to the decrease of fatigue life. Lower surface roughness and larger surface hardening rate may improve the creep feed grinding fatigue property of DD5.

Key words: DD5 super alloy, creep feed grinding, surface roughness, surface hardening rate, fatigue property, fracture mechanism

中图分类号:

TP182

靳淇超1, 2, 包虎子1, 李良万3, 汪文虎3, 张锦淇1, 叶子银1, 郭磊1. DD5缓进磨削表面粗糙度和硬化率对疲劳性能影响研究[J]. 中国机械工程, 2024, 35(08): 1472-1479.

JIN Qichao1, 2, BAO Huzi1, LI Liangwan3, WANG Wenhu3, ZHANG Jinqi1, YE Ziyin1, GUO Lei1. Research on Influences of Surface Roughness and Hardening Rate on Fatigue Property in DD5 Creep Feed Grinding[J]. China Mechanical Engineering, 2024, 35(08): 1472-1479.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://www.cmemo.org.cn/CN/10.3969/j.issn.1004-132X.2024.08.015

http://www.cmemo.org.cn/CN/Y2024/V35/I08/1472

参考文献

［1］孙晓峰, 金涛, 周亦胄, 等. 镍基单晶高温合金研究进展［J］. 中国材料进展, 2012, 31(12):1-11.
SUN Xiaofeng, JIN Tao, ZHOU Yizhou, et al. Research Progress of Nickel-base Single Crystal Superalloys［J］. Materials China, 2012, 31(12):1-11.
［2］窦学铮, 蒋立武, 宋尽霞, 等. 镍基单晶高温合金力学性能各向异性的研究进展［J］. 材料导报, 2022, 36(24):158-172.
DOU Xuezheng, JIANG Liwu, SONG Jinxia, et al. Research Progress on Anisotropy of Mechanical Properties for Nickel Based Single Crystal Superalloys［J］. Materials Reports, 2022, 36(24):158-172.
［3］张健, 王莉, 王栋, 等. 镍基单晶高温合金的研发进展［J］. 金属学报, 2019, 55(9):1077-1094.
ZHANG Jian, WANG Li, WANG Dong, et al. Recent Progress in Research and Development of Nickel-based Single Crystal Superalloys［J］. Acta Metallurgica Sinica, 2019, 55(9):1077-1094.
［4］蒋睿嵩, 汪文虎, 王增强, 等. 航空发动机涡轮叶片精密成形技术及其发展趋势［J］. 航空制造技术, 2016, 59(21):57-62.
JIANG Ruisong, WANG Wenhu, WANG Zengqiang, et al. Precision Forming Technology and Its Development Trend of Aeroengine Turbine Blade［J］. Aeronautical Manufacturing Technology, 2016, 59(21):57-62.
［5］杨忠学. IC10高温合金抗疲劳缓进磨削技术研究［D］. 西安：西北工业大学, 2019.
YANG Zhongxue. Research on Anti-fatigue Creep-feed Grinding Technology for IC10 Superalloy［D］. Xian：Northwestern Polytechnical University, 2019.
［6］金滩, 何训, 王其荣, 等. 向极限挑战的高性能磨削技术发展及其在航空制造领域的应用前景［J］. 航空制造技术, 2022, 65(9):20-33.
JIN Tan, HE Xun, WANG Qirong, et al. Development of High Performance Grinding Processes to Challenge Physical Limitations:Application Prospects in Aeronautical Manufacture Engineering［J］. Aeronautical Manufacturing Technology, 2022, 65(9):20-33.
［7］朱志成, 杨昭, 潘博, 等. 各向异性对IC10高温合金磨削表面完整性的影响［J］. 表面技术, 2023, 52(1):222-231.
ZHU Zhicheng, YANG Zhao, PAN Bo, et al. Effect of Anisotropy on Surface Integrity of IC10 Superalloy after Grinding［J］. Surface Technology, 2023, 52(1):222-231.
［8］ZHAO Shuangqun, XIE Xishan, SMITH G D, et al. Microstructural Stability and Mechanical Properties of a New Nickel-based Superalloy［J］. Materials Science and Engineering:A, 2003, 355(1/2):96-105.
［9］LIN Y C, CHEN Xiaomin, WEN Dongxu, et al. A Physically-based Constitutive Model for a Typical Nickel-based Superalloy［J］. Computational Materials Science, 2014, 83:282-289.
［10］贾新云, 陈升平, 宗毳, 等. DD5合金单晶双联整铸导向叶片的热工艺匹配性［J］. 金属热处理, 2022, 47(6):13-18.
JIA Xinyun, CHEN Shengping, ZONG Cui, et al. Thermal Process Matching of Single Crystal Double Casting Guide Vane of DD5 Alloy［J］. Heat Treatment of Metals, 2022, 47(6):13-18.
［11］曾曦, 黄永德, 简园园, 等. 铸态DD5单晶在热处理过程中的组织转变规律［J］. 精密成形工程, 2019, 11(5):166-172.
ZENG Xi, HUANG Yongde, JIAN Yuanyuan, et al. Microstructure Transformation Rule of As-cast DD5 Single Crystal during Heat Treatment［J］. Journal of Netshape Forming Engineering, 2019, 11(5):166-172.
［12］黄新春, 张定华, 姚倡锋, 等. 镍基高温合金GH4169磨削参数对表面完整性影响［J］. 航空动力学报, 2013, 28(3):621-628.
HUANG Xinchun, ZHANG Dinghua, YAO Changfeng, et al. Effects of Grinding Parameters on Surface Integrity of GH4169 Nickel-based Superalloy［J］. Journal of Aerospace Power, 2013, 28(3):621-628.
［13］WANG Junwei, XU Jijin, WANG Xiangfei, et al. A Comprehensive Study on Surface Integrity of Nickel-based Superalloy Inconel 718 under Robotic Belt Grinding［J］. Materials and Manufacturing Processes, 2019, 34(1):61-69.
［14］蔡明, 巩亚东, 屈硕硕, 等. 镍基单晶高温合金磨削表面质量及亚表面微观组织试验［J］. 东北大学学报(自然科学版), 2019, 40(3):386-391.
CAI Ming, GONG Yadong, QU Shuoshuo, et al. Experiment of Grinding Surface Quality and Subsurface Microstructure for Nickel-based Single Crystal Superalloy［J］. Journal of Northeastern University(Natural Science), 2019, 40(3):386-391.
［15］DING Wenfeng, XU Jiuhua, CHEN Zhenzhen, et al. Grindability and Surface Integrity of Cast Nickel-based Superalloy in Creep Feed Grinding with Brazed CBN Abrasive Wheels［J］. Chinese Journal of Aeronautics, 2010, 23(4):501-510.
［16］ZHANG Shuaiqi, YANG Zhongxue, JIANG Ruisong, et al. Effect of Creep Feed Grinding on Surface Integrity and Fatigue Life of Ni3Al Based Superalloy IC10［J］. Chinese Journal of Aeronautics, 2021, 34(1):438-448.
［17］王冬冬, 王波. GH4169抗疲劳表面砂带磨削工艺参数优化［J］. 航空制造技术, 2023, 66(21):125-131.
WANG Dongdong, WANG Bo. Optimization of Process Parameters for GH4169 Anti-fatigue Surface Abrasive Belt Grinding［J］. Aeronautical Manufacturing Technology, 2023, 66(21):125-131.
［18］LIU Enze, ZHENG Zhi, TONG Jian, et al. Study on High Cycle Fatigue Properties of DZ468 Superalloy［J］. Acta Metallurgica Sinica, 2010, 46(6):708-714.
［19］SUN Jianfei, WANG Tianming, SU Anpeng, et al. Surface Integrity and Its Influence on Fatigue Life when Turning Nickel Alloy GH4169［J］. Procedia CIRP, 2018, 71:478-483.
［20］王欣, 胡云辉, 王晓峰, 等. 喷丸强化对FGH96粉末高温合金疲劳性能应力集中敏感性的影响［J］. 航空制造技术, 2017, 60(13):48-53.
WANG Xin, HU Yunhui, WANG Xiaofeng, et al. Effect of Shot Peening on Fatigue Performance Stress-concentration Sensitivity of FGH96 Powder Metallurgy Superalloy［J］. Aeronautical Manufacturing Technology, 2017, 60(13):48-53.
［21］黄新春, 张定华, 姚倡锋, 等. 高效抗疲劳磨削加工技术研究［J］. 航空精密制造技术, 2011, 47(3):1-4.
HUANG Xinchun, ZHANG Dinghua, YAO Changfeng, et al. Research on High-efficient and Anti-fatigue Grinding Machining Technology［J］. Aviation Precision Manufacturing Technology, 2011, 47(3):1-4.
［22］LI Xun, WANG Yixuan, XU Rufeng, et al. Influence of Surface Integrity on Fatigue Behavior of Inconel 718 and Ti6Al4V Workpieces with CBN Electroplated Wheel［J］. The International Journal of Advanced Manufacturing Technology, 2019, 102(5):2345-2356.
［23］靳淇超, 曹帅帅, 汪文虎, 等. DD5镍基单晶高温合金缓进磨削表面完整性研究［J］. 西北工业大学学报, 2022, 40(1):189-198.
JIN Qichao, CAO Shuaishuai, WANG Wenhu, et al. Study on Surface Integrity of DD5 Nickel-based Single Crystal Super-alloy in Creep-feed Grinding［J］. Journal of Northwestern Polytechnical University, 2022, 40(1):189-198.
［24］NEUBER H. Theory of Notch Stresses［M］. Berlin:Springer Verlag, 1958:204-210.

[1]	贾志新, 张凯悦, 王津. 聚晶金刚石的混铁粉电火花加工方法研究[J]. 中国机械工程, 2023, 34(22): 2684-2692.
[2]	王明, 董海, 王柏何, 王峥, 王加威. 2.5D Cf/SiC刹车材料浮动磨削工艺试验研究[J]. 中国机械工程, 2023, 34(20): 2434-2441.
[3]	韩锐, 李秀红, 王嘉明, 李文辉, 程思源, 杨胜强, . 水平强制振动光整加工对TC4钛合金表面完整性参数的影响[J]. 中国机械工程, 2023, 34(17): 2037-2047.
[4]	田龙, 黄传真, 刘盾, 姚鹏, 刘含莲, 刘雪飞. 激光辅助水射流微铣削单晶β-Ga2O3衬底的实验研究[J]. 中国机械工程, 2023, 34(13): 1559-1567.
[5]	傅远韬, 文东辉, 孔凡志, 淦作昆, 成志超, . 线性液动压抛光加工的流场特性研究[J]. 中国机械工程, 2023, 34(11): 1306-1314.
[6]	鲁艳军, 关伟锋, 孙佳劲, 莫睿, 伍晓宇. 基于放电修锐的粗金刚石砂轮干式镜面磨削技术[J]. 中国机械工程, 2023, 34(09): 1052-1060.
[7]	王栋, 林洪旭, 赵静雯, 乔瑞勇, 张君宇, 赵睿. 高速切向车铣对18CrNiMo7-6钢表面完整性的影响[J]. 中国机械工程, 2023, 34(07): 812-820.
[8]	郝宇聪, 赵韡, 杨焘, 郭鹏, . 射流束切削时在边壁约束下的直径增大变形及加工表面质量研究[J]. 中国机械工程, 2022, 33(17): 2029-2037.
[9]	马廉洁, 李红双. 脆性材料机械加工表面粗糙度模型的研究进展[J]. 中国机械工程, 2022, 33(07): 757-768.
[10]	张晓博, 朱栋. 长窄型薄壁叶片的套料电解加工[J]. 中国机械工程, 2022, 33(07): 797-803，810.
[11]	章玉强, 胡中伟, 朱泽朋, 崔长彩, 陈铭欣, 谢斌晖, 李瑞萍. 硬脆性材料用柔性磨具研磨的加工表面粗糙度建模[J]. 中国机械工程, 2022, 33(07): 834-841.
[12]	雷勇, 赵威, 何宁, 李亮. TC17钛合金低温铣削表面粗糙度预测[J]. 中国机械工程, 2022, 33(05): 583-588.
[13]	李聪波, 龙云, 崔佳斌, 赵希坤, 赵德. 基于多源异构数据的数控铣削表面粗糙度预测方法[J]. 中国机械工程, 2022, 33(03): 318-328.
[14]	时强胜, 张小俭, 陈巍, 杨泽源, 严思杰, . 基于灰色关联度分析响应面法的橡胶软模端面抛磨表面粗糙度预测[J]. 中国机械工程, 2021, 32(24): 2967-2974.
[15]	姜云禄, 杨亮, 韩晓辉, 徐野, 陈怀宁, 蔡桂喜. 运行条件对不锈钢点焊疲劳性能影响及开裂分析[J]. 中国机械工程, 2021, 32(14): 1726-1731.