[1]朱立群,谷岸,刘慧丛,等.典型高强铝合金材料的点腐蚀坑前缘特征的研究[J].航空材料学报,2008,28(6):61-66.
Zhu Liqun,Gu An,Liu Huicong,et al.Study on Characters of Corrosion Advancing Edge of Typical High Strength Aluminum Alloys[J]. Journal of Aeronautical Materials,2008,28(6):61-66.
[2]李晗.2024铝合金薄板的热处理工艺与性能研究[D].西安:西北工业大学,2007.
[3]张川,姚卫星.铝合金预腐蚀剩余寿命的分形维数预测方法[J].中国机械工程,2013,24(17):2337-2340.
Zhang Chuan,Yao Weixing.Prediction of Residual Life of Pre-corrosion Aluminum Alloy with Fractal Dimension[J].China Mechanical Engineering, 2013,24(17):2337-2340.
[4]张有宏,吕国志,李仲,等.铝合金结构腐蚀疲劳裂纹扩展与剩余强度研究[J].航空学报,2007,28(2):332-335.
Zhang Youhong,Lü Guozhi,Li Zhong,et al.Investigation on Corrosion Fatigue Crack Growth and Residual Strength of Aluminum Alloy Structure[J]. Acta Aeronautica et Astronautica Sinica,2007,28(2):332-335.
[5]Jones K,Shinde S R,Paul N,et al.Effect of Prior Corrosion on Short Crack Behaviour in 2024-T3 Aluminum Alloy[J].Corrosion Science,2008,50(9):2588-2595.
[6]Li Xudong,Wang Xishu,Ren Huaihui,et al.Effect of Prior Corrosion State on the Fatigue Small Cracking Behavior of 6151-T6 Aluminum Alloy[J].Corrosion Science,20112,55(2):26-33.
[7]陈勃,刘建中,王浩伟,等.腐蚀预损伤铝合金的疲劳行为研究进展[J].失效分析与预防,2011,6(3):186-192.
Chen Bo,Liu Jianzhong,Wang Haowei,et al.Advance in Fatigue Behavior for Pre-corroded Aluminium Alloy[J].Failure Analysis and Prevention,2011,6(3):186-192.
[8]鲁连涛,盐泽和章,西野精一.研磨加工层对高碳铬轴承钢超长寿命疲劳行为的影响[J].机械工程学报,2007,43(2):115-121.
Lu Liantao,Shiozawa Kazuaki,Nishino Seiichi.Effect of Ground Layer on Ultra Long Life Fatigue Behaviour in High Carbon Chromium Bearing Steel[J].Chinese Journal of Mechanical Engineering,2007,43(2):115-121.
[9]Murakami Y,Kaneta M,Yatsuzuka Y.Analysis of Surface Crack Propagation in Lubricated Rolling Contact[J]. ASLE Transactions, 1985,28(1):60-68.
[10]DuQuesnay D L,Underhill P R,Britt H J.Fatigue Crack Growth from Corrosion Damage in 7075-T651 Aluminium Alloy under Air-craft Loading[J].International Journal of Fatigue,2003,25:371-377.
[11]Sankaran K K,Perez R,Jata K V.Effects of Pitting Corrosion on the Fatigue Behavior of Aluminum Alloy 7075-T6:Modeling and Experimental Studies[J].Materials Science and Engineering,2001,297(1/2):223-229.
[12]Lankford J. the Growth of Small Fatigue Cracks in 7075-T6 Aluminum[J].Fatigue and Fracture of Engineering Materials and Structures, 1982,5(3):233-248.
[13]Newman J C,Edwards P R.Short-crack Growth Behavior in an Aluminum Alloy-an AGARD Cooperative Test Programme[R]. Neuilly-sur-Seine,France:AGARD Report,1998.
[14]Dolley E J,Lee B,Wei R P.The Effect of Pitting Corrosion on Fatigue Life[J].Fatigue and Fracture of Engineering Materials and Structures,2000,23(7):555-560.
[15]Medved J J,Breton A M,Irving P E.Corrosion Pit Size Distributions and Fatigue Lives-a Sstudy of the EIFS Technique for Fatigue Design in the Presence of Corrosion[J].International Journal of Fatigue,2004,26(1):71-80.
[16]陈定海,穆志韬,朱做涛,等.腐蚀坑对疲劳裂纹扩展的影响分析[J].装备环境工程,2012,9(4):4-7.
Chen Dinghai,Mu Zhitao,Zhu Zuotao,et al.Analysis of Corrosion Pitting Effect on Fatigue Crack Growth[J].Equipment Environmental Engineering,2012,9(4):4-7.
[17]任克亮,吕国志.含腐蚀坑结构损伤演化评估过程[J].中国工程科学,2007,9(9):63-67.
Ren Keliang,Lu Guozhi.Damage Assessment Techniques for Pitting Corroded Structures[J].Engineering Sciences,2007,9(9):63-67.
[18]董妍,任克亮,刘平平,等.含广布腐蚀坑结构寿命评估方法[J].力学与实践,2011,33(3):46-49.
Dong Yan,Ren Keliang,Liu Pingping,et al.Multiplesite Corrosion Damage Assessment[J].Mechanics in Engineering,2011,33(3):46-49.
[19]刘建中,陈勃,叶序彬,等.含腐蚀预损伤铝合金2024-T62的疲劳断裂行为及基于断裂力学的寿命预测[J].航空学报,2011,32(1):107-116.
Liu Jianzhong,Chen Bo,Ye Xubing,et al.Fatigue and Crack Growth Behavior of Pre-corroded Aluminum Alloy 2024-T62 and Its Life Prediction Based on Fracture Mechanics[J].Acta Aeronautica et Astronautica Sinica,2011,32(1):107-116.
[20]Gruenberg K M,Craig B A,Hillberry B M,et al.Predicting Fatigue Life of Pre-corroded 2024-T3 Aluminum[J].International Journal of Fatigue,2004,26(6):629-640.
[21]HB7705-2001金属材料疲劳小裂纹扩展速率试验方法[S]. 北京:国防科学技术工业委员会,2001. |