PTFE/芳纶纤维编织衬垫自润滑关节轴承的黏接性能及摩擦学性能

李迎春1,2;邱明1,2;苗艳伟1   

  1. 1.河南科技大学,洛阳,471003
    2.机械装备先进制造河南省协同创新中心,洛阳,471003
  • 出版日期:2016-01-25 发布日期:2016-12-15
  • 基金资助:
    国家自然科学基金资助项目(51275155);河南省高校科技创新团队支持计划资助项目(13IRTSTHN025)

Bonding Behavior and Tribological Property for Self-lubricating Spherical  Plain  Bearings  with  PTFE/Kevlar  Woven Liners

Li  Yingchun1,2;Qiu  Ming1,2;Miao Yanwei1   

  1. 1.Henan University of  Science  and  Technology,Luoyang,Henan,471003
    2.Mechatronics Engineering Collaborative Innovation Center of Machinery Equipment Advanced Manufacturing,Luoyang,Henan,471003
  • Online:2016-01-25 Published:2016-12-15
  • Supported by:

摘要:

对PTFE/Kevlar纤维混合编织衬垫分别进行超声波处理、稀土CeO2处理后,制备了自润滑关节轴承,利用Instron5944型电子万能材料试验机和自制的高频摆动摩擦磨损试验机对关节轴承进行了剥离强度测试和摩擦磨损性能试验,考察了前处理工艺对关节轴承的黏接性能和摩擦学性能的影响,并采用扫描电镜(SEM)观察分析了衬垫表面的微观形貌变化,以探究轴承的摩擦学性能与衬垫形成PTFE转移膜的成膜性能之间的关系。结果表明,衬垫经改性前处理后,不仅提高了衬垫与基体的黏接性能,而且提高了轴承的摩擦学性能;轴承的摩擦学性能与其在摩擦磨损过程中形成PTFE转移膜的成膜性能之间存在一定的对应关系,即PTFE转移膜的形成越快,耐磨性、均匀连续性越好,在摩擦磨损过程中表现出较优的摩擦诱导成膜性能,其摩擦学性能也越优。

关键词: 关节轴承, 摩擦, 磨损, 衬垫, PTFE转移膜, 黏接

Abstract:

The  liners of hybrid PTFE/Kevlar  fabrics were modified with two different methods(ultrasonic wave treated and rare earth CeO2 treated).The peeling strength was measured using Instron5944 electronic universal material testing machine and hign frequency pendular friction wear testing machine,the  tribological  property was investigated using  the spherical plain bearing tester with high swaying frequency,and  worn surfaces observed by scanning electron microscope(SEM).The effects  of pretreatment methods on the bonding property and tribological property of spherical plain bearings and  the  relation  of thetribological property and film-forming behavior would be investigated.The results show that the bonding behavior of the modified bearings is  improved,and its tribological property  is improved as well.There is a correlation between the tribological property and film-forming behavior.When more smooth and continuous PTFE  transfer  film  is  formed in short time,
its tribological property is also better.

Key words: spherical plain bearing;friction;wear, liner;PTFE transfer film, bonding