水包油型乳化液钛合金TC4电火花加工特性研究

摘要/Abstract

摘要：

为解决钛合金在煤油介质中电火花加工效率低及在蒸馏水介质中加工表面质量差的问题,提出利用乳化剂将煤油和蒸馏水超声振动后形成水包油型乳化液作为工作介质的加工方法。分别以煤油、水包油型乳化液和蒸馏水为工作介质,对钛合金TC4进行放电加工试验,从加工效率、电极相对损耗率和表面质量三个方面,对比研究了不同工作介质中钛合金电火花加工的特性。试验结果表明：水包油型乳化液中的加工效率是煤油中加工效率的两倍左右,工件表面粗糙度值Ra比蒸馏水中的Ra值减小了15%~20%,加工后工件表面微裂纹较少,表面较平整,但其电极相对损耗率高。

关键词: 水包油型乳化液, 钛合金, 电火花加工, 加工效率

Abstract:

To solve the problems for TC4 EDM, such as lower machining efficiency in kerosene and bad surface quality in distilled water, the kerosene and emulsifier were added into distilled water and vibrated by ultrasound to form oil-in-water emulsion herein. To study the characteristics of three kind of dielectrics used in TC4 EDM, kerosene, oil-in-water emulsion and distilled water were used as working dielectrics to machine titanium alloy, they were compared in aspects of MRR, electrode wearing rate (EWR) and surface quality. Results show that: two times higher machining efficiency in oil-in-water emulsion can be obtained than in kerosene and the surface roughness is decreased 15%~20% than in distilled water. After machining in oil-in-water emulsion, there are less surface microcracks on the workpiece, and its surface smoothness is better than the others machined in kerosene and distilled water, but the EWR is higher.

Key words: oil-in-water emulsion, titanium alloy, electrical-discharge machining(EDM), material removal rate (MRR)

中图分类号:

TG662

薛荣媛, 刘志东, 王祥志, 邱明波, 田宗军. 水包油型乳化液钛合金TC4电火花加工特性研究[J]. 中国机械工程, 2014, 25(9): 1164-1168.

Xue Rongyuan, Liu Zhidong, Wang Xiangzhi, Qiu Mingbo, Tian Zongjun. Research on Titanium Alloy TC4 Electrical-discharge Machining Characteristics Using Oil-in-water Emulsion[J]. China Mechanical Engineering, 2014, 25(9): 1164-1168.

参考文献

[1]刘志东, 高长水. 电火花加工工艺及应用[M]. 北京: 国防工业出版社,2011.
[2]Chen S, Yan B, Huang F. Influence of Kerosene and Distilled Water as Dielectrics on the Electric Discharge Machining Characteristics of Ti-6A1-4V[J].Journal of Materials Processing Technology, 1999, 87(1):107-111.
[3]倪青. 蒸馏水介质中钛合金的电火花加工[J]. 湖北航天科技, 2007(2):34-37.
Ni Qing. Electrical Discharge Machining of Titanium Alloy in Distilled Water[J].Hubei Aerospace Science and Technology, 2007(2): 34-37.
[4]波林，普劳斯尼茨，奥康奈尔. 气液物性估算手册[M]. 赵红玲，王凤坤，陈圣坤,等，译. 北京: 化学工业出版社,2006.
[5]郑铸, 迟恩田. 钛合金水中电火花加工的研究[J]．航空制造技术, 1986(4):31-36. Zheng Zhu, Chi Entian. Study on Electric Discharge Machining of Titanium Alloy in Water[J]. Aeronautical Manufacturing Technology, 1989(4): 31-36.
[6]李明辉. 电火花加工理论基础[M]. 北京: 国防工业出版社,1989.
[7]陈文安, 刘志东, 王祥志, 等.钛合金TC4放电加工电极损耗研究[J]. 机械制造与自动化, 2012, 41(4):163-166.
Chen Wen’an, Liu Zhidong, Wang Xiangzhi, et al．Research on Tool Wear of Titanium Alloy(TC4) by EDM[J]．Machine Building & Automation, 2012, 41(4): 163-166.
[8]萧至君. 不同加工液(煤油, 蒸馏水, 混合液)对钛合金(Ti-6Al-4V)放电加工特性之影响[D]. 台北: 中央大学, 2000.
[9]魏引焕, 张晓燕. 电火花加工中干扰因素对加工质量的影响[J]. 陕西科技大学学报, 2005, 23(6): 96-100.
Wei Yinhuan, Zhang Xiaoyan. The Analyses of Factors Which Influence the Quality in Electrosparking[J]. Journal of Shaanxi University of Science & Technology, 2005, 23(6): 96-100.
[10]王怀志, 刘志东, 田宗军, 等. 钛合金TC4不同介质放电加工蚀除机理研究[J]．电加工与模具, 2012(1):24-28.
Wang Huaizhi, Liu Zhidong, Tian Zongjun, et al. Material Removal Mechanism of the Ti-6Al-4V EDM with Different Dielectrics[J]. Electromachining & Mould, 2012(1): 24-28.

[1]	翁剑, 庄可佳, 浦栋麟, 丁汉, . 基于机器学习和多目标算法的钛合金插铣优化[J]. 中国机械工程, 2021, 32(07): 771-777.
[2]	吴英龙, 宣海军, 单晓明, 付汝龙. 离心轮内部疲劳裂纹扩展及其无损定量表征[J]. 中国机械工程, 2021, 32(06): 658-665.
[3]	王晓铭1;张建超1;王绪平2;张彦彬2;罗亮3;赵伟4;刘波5;聂晓霖6;李长河1. 不同冷却工况下的磨削钛合金温度场模型及验证[J]. 中国机械工程, 2021, 32(05): 572-578,586.
[4]	刘志强, 赵杰, 王克环, 武永, 吕良星, 刘钢, 苑世剑, . [成形过程仿真优化与集成计算材料工程]钛合金热成形工艺形变与组织演变耦合多尺度仿真研究进展[J]. 中国机械工程, 2020, 31(22): 2678-2690,2698.
[5]	赵亭;肖继明;范思敏;杨振朝;杨福杰. TC4钛合金低频振动钻削切屑形态和钻削力研究[J]. 中国机械工程, 2020, 31(19): 2276-2282.
[6]	罗戈山;邹莱;黄云;龚明旺. 氧化铝空心球砂带磨削钛合金的材料去除及表面质量研究[J]. 中国机械工程, 2020, 31(19): 2363-2370.
[7]	李晓鹏, 王元刚, 刘宇, 王慧, 赵福令. 电蚀产物对微细电火花电极形状损耗影响的实验研究[J]. 中国机械工程, 2020, 31(15): 1815-1822,1889.
[8]	何耿煌, 鄢国洪, 李凌祥, 程程. [刀具及切削工艺]典型钛合金TC17车削过程鳞刺生成规律及其抑制措施[J]. 中国机械工程, 2020, 31(13): 1585-1592.
[9]	石晨;田业冰;范增华;周强. 钛合金表面多磁极耦合旋转磁场光整加工特性[J]. 中国机械工程, 2020, 31(12): 1415-1420.
[10]	鹿旭飞1,2;马良1,2;林鑫1,2;郑宇翔1,2. 激光立体成形TC4钛合金的热力场演化[J]. 中国机械工程, 2020, 31(10): 1246-1252.
[11]	陈俊宏1;温鹏1,2;常保华1,2;单际国1,2;都东1,2;程昊3. 钛合金激光清洗及其对激光焊接气孔的影响[J]. 中国机械工程, 2020, 31(04): 379-383.
[12]	梁旭;蔡重延;安庆龙;陈明. TC4铣削中超临界CO2混合油膜附水滴的冷却润滑性能[J]. 中国机械工程, 2020, 31(03): 328-335.
[13]	王峰1,2;赵建社1;刘鼎明1;范延涛1;田宗军1. 钛合金深窄槽可控振动辅助电解加工试验研究[J]. 中国机械工程, 2019, 30(20): 2395-2402.
[14]	王锋;张勇斌;刘广民;王卿;袁伟然;胡波. 甚高频共振式脉冲源放电蚀除[J]. 中国机械工程, 2019, 30(20): 2439-2446.
[15]	张利;黄一;陈国达;傅昱斐. 钛合金曲面磨粒流加工扰流流道仿真与试验研究[J]. 中国机械工程, 2019, 30(05): 519-527.