Al7.8Co20.6Cr12.2Fe11.5Ni40.7Ti7.2高熵超合金的摩擦磨损行为研究

doi:10.3969/j.issn.1004-132X.2023.13.006

摘要/Abstract

摘要： 使用真空非自耗电弧熔炼技术制备了Al7.8Co20.6Cr12.2Fe11.5Ni40.7Ti7.2高熵超合金，表征了该合金的显微结构和力学性能，考察了该合金在硝酸介质和高温环境中的摩擦磨损性能。结果表明：该高熵超合金的显微组织以树枝晶为主，其维氏硬度、屈服强度、抗压强度和断裂韧性分别为422±8 HV0.2、991±32 MPa、2121±197 MPa和49.5±0.1 MPa·m0.5。在硝酸介质中，该高熵超合金的抗腐蚀性能优于0Cr17Ni7Al不锈钢，在硝酸介质中的摩擦因数和磨损率均低于干摩擦状态，主要是因为磨损表面氧化物的生成降低了摩擦因数并提高了抗磨损性能。在高温环境中，温度对其摩擦因数有显著的影响；随着温度的升高，摩擦因数和磨损率均呈下降趋势。不同温度下磨损表面的氧含量具有显著的差异，温度越高，其氧含量越高。

关键词: 高熵超合金, 腐蚀磨损, 高温磨损, 力学性能, 硝酸腐蚀

Abstract: Al7.8Co20.6Cr12.2Fe11.5Ni40.7Ti7.2 high entropy superalloy was prepared by vacuum arc melting in argon atmosphere. The microstructure and mechanics properties of the alloy were characterized. The friction and wear properties of the high entropy superalloy in nitric acid and at high-temperature environments were evaluated. Results show that the microstructure of the high-entropy superalloy is mainly composed of dendrites. The Vickers hardness， yield strength， compressive strength and fracture toughness of the high entropy superalloy are as 422±8 HV0.2， 991±32 MPa， 2121±197 MPa and 49.5±0.1 MPa·m0.5， respectively. The high entropy superalloy has better corrosion resistance than that of 0Cr17Ni7Al in nitric acid. The friction coefficient and wear rate of the high-entropy superalloy in nitric acid are lower than those in dry sliding. The main reason is that the formation of oxide film on the worn surface reduces the friction coefficient and improves the wear resistance in the high temperature friction processes. In high-temperature environments， the temperature has a significant effect on the friction coefficient. The friction coefficient and wear rate decrease with the increasing temperature and the oxygen contents of the worn surfaces at different temperatures have significant difference， as the oxygen contents increase with the temperature increases.

Key words: high-entropy superalloy, corrosion wear, high-temperature wear, mechanics property, nitric acid corrosion

中图分类号:

TG115.5

李光俊, 段宏, 徐磊, 阚琛, 刘忠亮, 高晓东. Al7.8Co20.6Cr12.2Fe11.5Ni40.7Ti7.2高熵超合金的摩擦磨损行为研究[J]. 中国机械工程, 2023, 34(13): 1568-1575.

LI Guangjun, DUAN Hong, XU Lei, KAN Chen, LIU Zhongliang, GAO Xiaodong. Research on Friction and Wear Behaviors of Al7.8Co20.6Cr12.2Fe11.5Ni40.7Ti7.2 High-entropy Superalloy[J]. China Mechanical Engineering, 2023, 34(13): 1568-1575.

参考文献

［1］ADIL S， SURAJ M V， PILLARI L K， et al. On the Effect of Fe in L12 Strengthened Al-Co-Cr-Fe-Ni-Ti Complex Concentrated Alloy［J］. Materialia， 2020， 14：100909.
［2］TSAO T K， YEH A C， MURAKAMI H. The Microstructure Stability of Precipitation Strengthened Medium to High Entropy Superalloys［J］. Metallurgical and Materials Transactions A， 2017， 48：2435-2442.
［3］WANG X Q， CARTER L N， PANG B， et al. Microstructure and Yield Strength of SLM-fabricated CM247LC Ni-superalloy［J］. Acta Materialia， 2017， 128：87-95.
［4］PRAVEEN S， KIM H S. High-entropy Alloys：Potential Candidates for High-temperature Applications—an Overview［J］. Advanced Engineering Materials， 2017， 20（1）：1700645.
［5］HUANG E W， LIAW P K. High-temperature Materials for Structural Applications：New Perspectives on High-entropy Alloys， Bulk Metallic Glasses， and Nanomaterials［J］. MRS Bulletin， 2019， 44：847-853.
［6］LI W D， XIE D， LI D Y， et al. Mechanical Behavior of High-entropy Alloys［J］. Progress in Materials Science， 2021， 118：100777.
［7］CHUANG M H， TSAI M H， WANG W R， et al. Microstructure and Wear Behavior of AlxCo1.5CrFeNi1.5Tiy High-entropy Superalloys［J］. Acta Materialia， 2011， 59（16）：6308-6317.
［8］TSAO T K， YEH A C， KUO C M， et al. High Temperature Oxidation and Corrosion Properties of High Entropy Superalloys［J］. Entropy， 2016， 18（2）：62-74.
［9］TSAO T K， YEH A C， KUO C M， et al. On the Superior High Temperature Hardness of Precipitation Strengthened High Entropy Ni-based Alloys［J］. Advanced Engineering Materials， 2017， 19（1）：1600475.
［10］TAKEUCHI A， INOUE A. Classification of Bulk Metallic Glasses by Atomic Size Difference， Heat of Mixing and Period of Constituent Elements and Its Application to Characterization of the Main Alloying Element［J］. Materials Transactions， 2005， 46（12）：2817-2829.
［11］ZHU S Y， CHENG J， QIAO Z H， et al. High Temperature Solid-lubricating Materials：a Review［J］. Tribology International， 2019， 133：206-223.
［12］ERDOAN A， GK M S， ZEYTIN S. Analysis of the High-temperature Dry Sliding Behavior of CoCrFeNiTi0.5Alx High-entropy Alloys［J］. Friction， 2020， 8：198-207.
［13］CHEN L J， BOBZIN K， ZHOU Z， et al. Wear Behavior of HVOF-sprayed Al0.6TiCrFeCoNi High Entropy Alloy Coatings at Different Temperatures［J］. Surface & Coatings Technology， 2019， 358：215-222.

[1]	周后明, 陈皓月, 李神贵. 基于梯度结构的Al2O3/ZrO2陶瓷刀具材料的制备及其力学性能[J]. 中国机械工程, 2023, 34(10): 1199-1207.
[2]	高恺, 李坤, 顾红历, . 镀锌量对低合金钢/5052铝合金感应静压焊接头微观组织与力学性能的影响[J]. 中国机械工程, 2023, 34(10): 1220-1229.
[3]	杨硕, 张杰, 孔宁, 王浩威, 王晓宇, 庄原. 航天用大展收比豆荚结构变形规律模型及其仿真验证[J]. 中国机械工程, 2023, 34(07): 780-788.
[4]	张岩, 黄传真, 刘含莲. 氮化碳基陶瓷刀具材料的制备与力学性能研究[J]. 中国机械工程, 2023, 34(03): 352-358，368.
[5]	方学伟, 蒋笑, 王喆, 武晓康, 黄科. ER120S-G高强钢电弧增材制造的工艺优化[J]. 中国机械工程, 2023, 34(02): 218-225.
[6]	蒋创宇, 张保强, 陈云, 王存福, 罗华耿, 胡杰翔, 曹龙超. Gyroid结构力学性能及数值收敛性研究[J]. 中国机械工程, 2022, 33(23): 2790-28000.
[7]	焦晨, 晁龙, 朱磊, 沈理达, 梁绘昕, 戴宁, 王长江, 孙骏. 面向骨科植入物的仿生多孔结构设计与制造方法[J]. 中国机械工程, 2022, 33(23): 2844-2850.
[8]	汤永锋, 路平, 刘斌, 江开勇, 颜丙功, 刘嘉伟, 韩伟, . 不同梯度变化方式的不规则多孔结构设计与力学性能分析[J]. 中国机械工程, 2022, 33(23): 2859-2866.
[9]	张帅, 陈照强, 肖光春, 衣明东, 张静婕, 周婷婷, 许崇海. Si3N4/TiC/ZrSi2陶瓷刀具裂纹愈合性能研究[J]. 中国机械工程, 2022, 33(19): 2288-2297.
[10]	曾寿金, , 李传生, 刘广, 许明三, 李涤尘. 选区激光熔化梯度多孔支架力学性能和能量吸收研究[J]. 中国机械工程, 2022, 33(19): 2364-2371.
[11]	张志彬, 张舒研, , 鲁楠, 陈永雄, 梁秀兵. AlNiZr非晶纳米晶复合涂层的腐蚀磨损行为研究[J]. 中国机械工程, 2022, 33(12): 1435-1443.
[12]	仲杨, 秦晓波, 郑志镇, 李建军, 王承. 石化容器用2.25Cr-1Mo-0.25V钢的CMT电弧熔丝增材制造工艺及组织性能研究[J]. 中国机械工程, 2022, 33(10): 1251-1259.
[13]	郑宇, 郭策, 马耀鹏, 管吉钢. 仿生多层级柔性轻质结构的设计、制备及力学性能分析[J]. 中国机械工程, 2021, 32(23): 2876-2882.
[14]	张志雄, 章俊涛, 韩建超, 张长江, 张树, 王涛. 马氏体组织Ti-6Al-4V钛合金多向等温锻造组织演变及力学性能强化研究[J]. 中国机械工程, 2021, 32(22): 2739-2748.
[15]	柯庆镝, 姜丰, 张鹏, 田常俊, 秦小州. 基于修复涂层力学性能影响规律的再制造毛坯表面污染物状态评估[J]. 中国机械工程, 2021, 32(19): 2340-2347,2356.