弱刚性构件磁流变抛光变形机理与抑制技术研究

doi:10.3969/j.issn.1004-132X.2022.18.005

摘要/Abstract

摘要： 弱刚性平面构件对应力极其敏感，加工后平面度难以保证，为解决该问题，提出通过磁流变抛光工艺改善工件的平面度。通过有限元仿真，阐明弱刚性构件磁流变抛光变形的机理，提出残余应力的不对称释放是造成工件变形的主要原因，并建立加工过程中工件变形预测模型。仿真结果表明，采用单面加工时，变形为9.5 μm；采用翻面加工时，变形为0.7 μm。根据仿真中工件变形的情况，提出了翻面加工的策略，并通过实验进行验证。实验结果表明，单面加工时，工件变形严重，而采用翻面加工时，变形会产生回复现象，从而使得工件平面度得到有效收敛。进而，提出了弱刚性构件磁流变修形抑制技术，即通过翻面等量材料去除实现工件表面残余应力的对称释放，并在200 mm、厚2 mm的纯铜弱刚性平面构件上应用该技术，两个面的平面度PV值分别从4.6 μm和5.9 μm降低到2.0 μm。

关键词: 弱刚性平面构件, 磁流变抛光, 残余应力, 平面度

Abstract: Weak stiffness components were sensitive to the stress, and it was hard to guarantee the flatness after machining. To solve this problem, A MRF process was proposed to improve the flatness. The deformation mechanism of the components was clarified, and the residual stress relaxation was considered as the main cause of the deformations, which was predicted by an established model. The simulation results show that the deformations are about 9.5 μm by single-side machining, while the deformations are about 0.7 μm by turning over machining. Thus, the machining strategy by turning over was proposed based on the simulation deformation results. Experiments were conducted to verify the simulation. The results reveal that serious deformations happen by single-side machining, while the deformations recover by turning over machining, and the flatness converged efficiently. By the turning over machining strategy, the flatness peak and valley(PV) value reduce from 4.6 μm and 5.9 μm to 2.0 μm respectively on a 200×2 mm weak stiffness flat component of copper.

Key words: weak stiffness component, magnetorheological finishing（MRF）, residual stress, flatness

中图分类号:

TH161.12

潘博, 康仁科, 贺增旭, 李凯隆, 张云飞, 黄文, 郭江. 弱刚性构件磁流变抛光变形机理与抑制技术研究[J]. 中国机械工程, 2022, 33(18): 2190-2196.

PAN Bo, KANG Renke, HE Zengxu, LI Kailong, ZHANG Yunfei, HUANG Wen, GUO Jiang. Investigation of Deformation Mechanism and Suppression Method of Weak Stiffness Components by Magnetorheological Finishing[J]. China Mechanical Engineering, 2022, 33(18): 2190-2196.

参考文献

［1］WANG J, ZHOU N, LI B, et al. Fabrication of Nanocrystalline Copper by Explosive Loading and Its Dynamic Mechanics Properties［J］. Combustion, Explosion, and Shock Waves, 2011, 47(3):369-373.
［2］JU K, DUAN C, KONG J, et al. Prediction of Clamping Deformation in Vacuum Fixture-workpiece System for Low-rigidity Thin-walled Precision Parts Using Finite Element Method［J］. The International Journal of Advanced Manufacturing Technology, 2020, 109(7/8):1895-1916.
［3］CHEN Y, HUANG X J, KONG J X. Research on Subsurface Deformed Layer in Ultra-precision Cutting of Single Crystal Copper by Focused Ion Beam Etching Method［J］. Journal of Physics, 2018, 986(1):12037.
［4］PAN B, KANG R, GUO J, et al. Precision Fabrication of Thin Copper Substrate by Double-sided Lapping and Chemical Mechanical Polishing［J］. Journal of Manufacturing Processes， 2019, 44:47-54.
［5］王嘉琪，肖强. 磁流变抛光技术的研究进展［J］. 表面技术, 2019, 48(10):317-328.
WANG Jiaqi, XIAO Qiang. Research Progress of Magnetorheological Polishing Technology［J］. Surface Technology, 2019, 48(10):317-328.
［6］沙树静，胡锦飞，张和权. 磁流变抛光技术发展［J］. 机械工程师，2018(7):5-8.
SHA Shujing, HU Jinfei, ZHANG Hequan. New Progress of Magnetorheological Finishing［J］. Mechanical Engineer，2018(7):5-8.
［7］LI L, ZHENG L, DENG W, et al. Optimized Dwell Time Algorithm in Magnetorheological Finishing［J］. The International Journal of Advanced Manufacturing Technology， 2015, 81(5/8):833-841.
［8］曾育伟，李圣怡，戴一帆，等. KDP晶体的磁流变抛光工艺研究［J］. 航空精密制造技术， 2012, 48(4):6-8.
ZENG Yuwei, LI Shengyi, DAI Yifan, et al. Research on Magnetorheological Polishing Process of KDP Crystal［J］. Aviation Precision Manufacturing Technology， 2012, 48(4):6-8.
［9］KORDONSKI W, GORODKIN S. Material Removal in Magnetorheological Finishing of Optics［J］. Applied Optics, Optical Technology and Biomedical Optics, 2011, 50(14):1984-1994.
［10］DAI Y, HU H, PENG X, et al. Research on Error Control and Compensation in Magnetorheological Finishing［J］. Applied Optics， 2011, 50(19):3321-3329.
［11］MIAO C, SHAFRIR S N, LAMBROPOULOS J C, et al. Shear Stress in Magnetorheological Finishing for Glasses［J］. Applied Optics, Optical Technology and Biomedical Optics, 2009, 48(13):2585-2594.
［12］戴一帆，石峰，彭小强，等. 光学镜面磁流变确定性修形的实现［J］. 光学学报，2010, 30(1):198-205.
DAI Yifan, SHI Feng, PENG Xiaoqiang, et al. Deterministic Figuring in Optical Machining by Magnetorheological Finishing［J］. Acta Optica Sinica，2010, 30(1):198-205.
［13］ZHANG Y, FANG F, HUANG W, et al. Polishing Technique for Potassium Dihydrogen Phosphate Crystal Based on Magnetorheological Finishing［J］. Procedia CIRP，2018, 71:21-26.
［14］ZHANG P, DONG Y Z, CHOI H J, et al. Reciprocating Magnetorheological Polishing Method for Borosilicate Glass Surface Smoothness［J］. Journal of Industrial and Engineering Chemistry，2020, 84:243-251.
［15］GUPTA M K, DINAKAR D, CHHABRA I M, et al. Experimental Investigation and Machine Parameter Optimization for Nano Finishing of Fused Silica Using Magnetorheological Finishing Process［J］. Optik，2021, 226:165908-1-12.
［16］郑立功，李龙响，王孝坤，等. 磁流变抛光系统去除函数的原点位置标定［J］. 光学精密工程, 2017, 25(1):8-14.
ZHENG Ligong, LI Longxiang, WANG Xiaokun, et al. Coordinate-origin Calibration of Removal Function in Magnetorheological Finishing［J］. Optics and Precision Engineering, 2017, 25(1):8-14.
［17］JUNG B, JANG K, MIN B, et al. Magnetorheological Finishing Process for Hard Materials Using Sintered Iron-CNT Compound Abrasives［J］. International Journal of Machine Tools and Manufacture, 2009, 49(5):407-418.
［18］彭小强，戴一帆，李圣怡. 磁流变抛光的材料去除数学模型［J］. 机械工程学报, 2004,40(4):67-70.
PENG Xiaoqiang, DAI Yifan, LI Shengyi. Material Removal Model of Magnetorheological Finishing［J］. Chinese Journal of Mechanical Engineering, 2004, 40(4):67-70.
［19］尹韶辉，邓子默，郭源帆，等. 单晶碳化硅的电磁场励磁大抛光模磁流变抛光［J］. 表面技术, 2020, 49(10):309-315.
YIN Shaohui, DENG Zhimo, GUO Yuanfan, et al. Magnetorheological Polishing Using Large Polishing Tool Excited by Electromagnetic Field for Silicon Carbide Wafer［J］. Surface Technology, 2020, 49(10):309-315.
［20］肖晓兰，阎秋生，潘继生，等. 陶瓷球高效超光滑磁流变柔性抛光新工艺研究［J］. 表面技术, 2019, 48(2):268-274.
XIAO Xiaolan, YAN Qiusheng, PAN Jisheng, et al. A Novel Polishing Method for High Precision Ceramic Balls Based on Magnetorheological Polisher［J］. Surface Technology, 2019, 48(2):268-274.
［21］徐超，胡皓，彭小强，等. 复杂曲面铝反射镜磁流变抛光工艺优化［J］. 航空学报, 2021, 42(10):524914-1-10.
XU Cao, HU Hao, PENG Xiaoqiang, et al. Optimization of Magnetorheological Polishing Process for Aluminum Mirror with Complex Surface［J］. Acta Aeronautica et Astronautica Sinica,2021, 42(10):524914-1-10.
［22］葛坤鹏，李圣怡，胡皓. 铝合金反射镜磁流变抛光表面质量控制的参数优化［J］. 纳米技术与精密工程,2017, 15(2):151-157.
GE Kunpeng, LI Shengyi, HU Hao. Parameters Optimization of Surface Quality Control on Magnetorheological Finishing for Aluminum Alloy Mirror［J］. Nanotechnology and Precision Engineering,2017, 15(2):151-157.
［23］唐小会，吉方，陈华，等. 基于华中数控的PKC-1000P2磁流变抛光机床控制系统设计与开发［J］. 制造技术与机床,2017(11):48-50.
TANG Xiaohui, JI Fang, CHEN Hua, et al. Design and Development of Control System of PKC1000-P2MRF Machine Based on HNC［J］. Manufacturing Technology & Machine Tool,2017(11):48-50.
［24］宋辞. 离轴非球面光学零件磁流变抛光关键技术研究［D］. 长沙:国防科学技术大学, 2012.
SONG Ci. Study on the Key Techniques of Magnetorheological Finishing for Off-axis Aspheric Optical Elements［D］. Changsha:National University of Defense Technology, 2012.
［25］HUANG X, SUN J, LI J. Finite Element Simulation and Experimental Investigation on the Residual Stress-related Monolithic Component Deformation［J］. International Journal of Advanced Manufacturing Technology, 2015, 77:1035-1041.

[1]	王东峰, 袁巨龙, 王燕霜, 程勇杰, 吕冰海. 轴承沟道表面完整性研究进展[J]. 中国机械工程, 2022, 33(18): 2143-2160.
[2]	周嘉利, 程延海, 陈永雄, 梁秀兵, 白成杰, 杜望. 激光熔覆工艺参数对铁基双层涂层组织和残余应力的影响[J]. 中国机械工程, 2022, 33(12): 1418-1426，1434.
[3]	易军, 龚志锋, 易涛, 周炜, . 齿根过渡圆弧对全齿槽成形磨削温度和残余应力影响的研究[J]. 中国机械工程, 2022, 33(11): 1278-1286.
[4]	张鹏, 曹泽泽, 寇淑清, 王涛, 郭继保, 李金哲, 吴磊. 组合式凸轮轴径向滚花装配机理及连接强度研究[J]. 中国机械工程, 2022, 33(06): 664-671.
[5]	刘恒, 王连东, 王晓迪, 刘超, . 管坯大变形自由推压缩径残余应力的研究[J]. 中国机械工程, 2021, 32(11): 1354-1360.
[6]	张银霞1;杨鑫1;原少帅1;朱建辉2;王栋1. 18CrNiMo7-6钢高速外圆磨削的残余应力[J]. 中国机械工程, 2021, 32(05): 540-546.
[7]	李慎旺1;张帆1;解丽静2. 复合铣削轨迹对表面质量的影响[J]. 中国机械工程, 2020, 31(10): 1219-1224.
[8]	李国龙1;谢天明1;任唯贤1;崔岗卫2. 横梁蠕变松弛对龙门镗铣床运动精度可靠性的影响建模[J]. 中国机械工程, 2020, 31(08): 944-951.
[9]	唐凯1;周留成2;何卫峰2;王文健1;郭俊1;刘启跃1. 激光冲击强化对LZ50车轴钢疲劳性能影响试验研究[J]. 中国机械工程, 2020, 31(03): 267-273.
[10]	赵相吉, 师陆冰, 王文健, 郭俊, 刘启跃. [表面强化及损伤机理]硌伤形貌对车轮材料滚动接触疲劳特性的影响[J]. 中国机械工程, 2019, 30(03): 278-283.
[11]	徐路遥;李蓓智;杨建国. 考虑硬度的高弹性合金钢3J33微细特征磨削仿真分析及实验研究[J]. 中国机械工程, 2019, 30(01): 17-21.
[12]	黄潇1,2;曹子文2;常明1;邹世坤2. 激光冲击强化对TC4钛合金单面修饰激光焊接接头疲劳性能的影响[J]. 中国机械工程, 2018, 29(01): 104-109.
[13]	徐兰英1;伍强2;覃孟扬1;汤勇3. 轴承圈加热切削加工表面质量研究[J]. 中国机械工程, 2017, 28(19): 2325-2331.
[14]	谢国贞1,2,3;吴运新1,2,3;龚海1,2,3;李晨4;刘瑶琼1,4;姬浩4;张伟4. 轮廓法测试残余应力中的数据处理[J]. 中国机械工程, 2017, 28(15): 1778-1783.
[15]	苗恩铭, 徐建国, 吕玄玄, 魏新园. 数控机床工作台误差综合补偿方法研究[J]. 中国机械工程, 2017, 28(11): 1326-1332.