热处理对TC11/LF6异种金属摩擦焊质量的影响

中国机械工程

热处理对TC11/LF6异种金属摩擦焊质量的影响

张昌明1;许林青1;张会1;侯军才1;余少军2

1.陕西理工大学，汉中，723001
2.汉中双戟摩擦焊接制造技术有限公司，汉中，723001

出版日期:2016-09-10 发布日期:2016-09-18
基金资助:
陕西省教育厅产业化项目（15JF014）

Effects of Heat Treatmant on Formation and Mechanical Properties Quality of TC11 and LF6 Dissimilar Metal Friction Welding Seam

Zhang Changming1;Xu Linqing1;Zhang Hui1;Hou Juncai1;Yu Shaojun2

1.Shaanxi Sci-Tech University,Hanzhong,Shaanxi,723001
2.Hanzhong Shuangji Friction Welding Manufacture Technology Co. Ltd.,Hanzhong,Shaanxi,723001

Online:2016-09-10 Published:2016-09-18

摘要/Abstract

摘要： 对TC11/LF6钛铝异种金属进行了连续驱动摩擦焊接工艺及其焊后热处理工艺的研究，观察了热处理前后焊接接头焊合区微观组织并测定了试样力学性能。研究结果表明：未经热处理的焊接接头晶粒较为粗大，有明显的晶间化合物产生，接头显微硬度较高；经280℃退火1h后，焊接接头晶粒均匀细化，焊接界面产生较薄的不连续扩散层；热处理后接头晶粒明显细化,抗弯强度提高10.7%，显微硬度下降38%。通过组织和力学性能综合分析，得到最优化的TC11/LF6连续驱动摩擦焊接工艺参数。

关键词: TC11钛合金, LF6铝合金, 连续驱动摩擦焊, 焊后热处理

Abstract: The continuous drive friction welding and post-weld heat treatment process of TC11 titanium alloy and LF6 stain resistant aluminum alloy were studied. The microstructures of welding zone before and after heat treatment were observed, and the mechanical properties were tested. The conclusions are as follows: before heat treatment, the grain size of weld zone is coarsened; intermetallic compounds may be observed clearly and the micro Vickers hardness increases. A discontinuous thin diffusion layer forms in the TC11/LF6 welding interface after heat treatment at 280℃. After heat treatment, the grain size of weld zone is fine, the bending strength increases by 10.7%, and the micro Vickers hardness decreases by 38%. The optimal friction wilding parameters were determined applying the bending tests and microstructure analysis.

Key words: TC11-alloy, LF6-alloy, continuous drive friction welding； post weld heat treatment

中图分类号:

TG453.9

张昌明, 许林青, 张会, 侯军才, 余少军. 热处理对TC11/LF6异种金属摩擦焊质量的影响[J]. 中国机械工程.

Zhang Changming, Xu Linqing, Zhang Hui, Hou Juncai, Yu Shaojun. Effects of Heat Treatmant on Formation and Mechanical Properties Quality of TC11 and LF6 Dissimilar Metal Friction Welding Seam[J]. China Mechanical Engineering.

参考文献

[1]白建红,傅莉,杜随更.钛合金/纯铝异种金属摩擦焊接工艺[J].焊接学报,2006,27(11):50-52.

Bai Jianhong, Fu Li, Du Suigeng. Friction Welding Technology between Titanium Alloy and Pure Aluminum[J].Transactions of the China Welding Institution,2006,27(11):50-52.

[2]黄鹏飞,卢振洋,高文宁,等.钢铝异种金属的低能量焊接法[J].机械工程学报,2009,45(11):295-298.

Huang Pengfei, Lu Zhenyang, Gao Wenning, et al.Low Energy Welding Technology in Bonding Steel with Aluminum.[J].Journal of Mechanical Engineering,2009,45(11):295-298.

[3]吉玲.钢铝异种金属连接方法现状分析[J].电焊机,2009,39(12):102-104.

Ji Ling. Analysis about the Jointing Status for Dissimilar Materials of Steel with Aluminum[J]. Electric Welding Machine，2009,39(12):102-104.

[4]胡经洪.Ti/Al的交流TIG焊接工艺[J].焊接,2002(5):28-30.

Hu Jinghong. Alternating Current TIG Welding Proce-dure Ti/Al[J]. Welding & Joining,2002(5):28-30.

[5]Chen Y C,Nakata K. Microstructural Characteriza-tion and Mechanical Properties in Friction Stir Welding of Aluminum and Titanium Dissimilar Alloys[J].Materials & Design,2009,30(3):469-474.

[6]陈国庆，冯吉才，何景山，等.TiAl基合金及其连接技术的研究进展[J].焊接,2007(1):16-20.

Chen Guoqing， Feng Jicai, He Jingshan, et al. Research Progress in Bonding Technology of TiAl-based Alloys[J].Welding & Joining,2007(1):16-20.

[7]Kimura, M, Nakamura, S, Kusaka, M, et al. Mechanical Properties of Friction Welded Joint between Ti-6Al-4V Alloy and Al-Mg Alloy (AA5052)[J].Science and Technology of Welding & Joining, 2005, 10(6), 666-672.

[8]傅莉, 杜随更, 白建红.TC4钛合金与LD10铝合金感应摩擦焊接头的组织与性能[J].中国有色金属学报. 2007,17(2):228-232.

Fu Li, Du Suigeng, Bai Jianhong.Microstructures and Properties of Induction Friction Welded Joint of TC4 Ti Alloy and LD10 Al Alloy[J].The Chinese Journal of Nonferrous Metals,2007,17(2):228-232.

[9]马志鹏,张旭昀,郭光伟.钛合金与铝合金异种金属焊接研究现状[J].兵器材料科学与工程,2014,37(5):128-132.

Ma Zhipeng， Zhang Xuyun, Guo Guangwei. Research Status of Welding of Ti/Al Dissimilar Alloy[J]. Ordnance Material Science and Engineering,2014,37(5):128-132.