Ti-6Al-4V燕尾榫结构微动疲劳裂纹萌生及扩展行为研究

摘要/Abstract

摘要：

针对Ti-6Al-4V钛合金燕尾榫连接结构在不同载荷下的微动疲劳现象，采用榫形微动疲劳试验进行研究，并对裂纹萌生扩展、微动磨损及断口进行分析。结果表明，微动疲劳使构件疲劳寿命显著降低约70%；疲劳载荷对微动裂纹扩展的影响比对裂纹萌生的影响更大；微动疲劳裂纹起始于接触面边缘，与接触表面约成45°角，裂纹扩展到60~150μm后转向与接触表面垂直；微动疲劳断口形貌表面在微动磨损区具有多个裂纹源点，但只有一个主裂纹形成。

关键词: Ti-6Al-4V钛合金, 燕尾榫, 微动疲劳, 微动磨损

Abstract:

Fretting fatigue tests were conducted on the Ti-6Al-4V Ti alloy dovetail joint to investigate fretting cracks and wear under various load levels.The results indicate that the fatigue life is significantly reduced due to fretting of the dovetail joint.The fatigue loading has more influence on crack propagation than on crack initiation.The fretting cracks originate at the edge of the contact surface and orientate at 45°and stayed for 60~150μm,then propagate nearly perpendicular to the surface until fracture.The fracture surface shows that multiple cracking at contact surface but only one main crack dominated.

Key words: Ti-6Al-4V , alloy;dovetail joint;fretting fatigue;fretting wear

中图分类号:

TG115.5

俞树荣, 王洁璐, 李淑欣, 宋伟. Ti-6Al-4V燕尾榫结构微动疲劳裂纹萌生及扩展行为研究[J]. 中国机械工程, 2015, 26(24): 3386-3390.

Yu Shurong, Wang Jielu, Li Shuxin, Song Wei. Study on the Initiation and Propagation of Fretting Fatigue Crack on the Ti-6Al-4V Alloy Dovetail Joint[J]. China Mechanical Engineering, 2015, 26(24): 3386-3390.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://www.cmemo.org.cn/CN/

http://www.cmemo.org.cn/CN/Y2015/V26/I24/3386

参考文献

[1]孔润祥,周祥英.汽轮机叶片根部的微动失效[J]. 热力透平,1993(2):45-49.
Kong Runxiang,Zhou Xiangying.Fretting Failure of Turbine Blade Root[J].Thermal Turbine,1993(2):45-49.
[2]何明鉴.机械构件的微动疲劳[M].北京:国防工业出版社,1994.
[3]沈明学,彭金方,郑健峰,等.微动疲劳研究进展[J].材料工程,2010(12):86-91.
Shen Mingxue,Peng Jinfang,Zheng Jianfeng,et al.Study and Development of Fretting Fatigue[J].Journal of Materials Engineering, 2010(12): 86-91.
[4]周仲荣, Vincent L．微动磨损[M]．北京: 科学出版社, 2002.
[5]Waterhouse R B. Fretting Fatigue[M]. London: Applied Science Publishers Ltd.,1981.
[6]Nowell D, Dini D, Hills D A. Recent Developments in the Understanding of Fretting Fatigue[J]. Engineering Fracture Mechanics,2006, 73(2): 207-222.
[7]刘道新, 何家文. 微动疲劳影响因素及钛合金微动疲劳行为[J]. 航空学报, 2001, 22(5): 454-457.
Liu Daoxin, He Jiawen. Review of Factors that Influence Fretting Fatigue(FF) and Investigation on FF Behavior of Ti-Alloy[J]. Acta Aeronautica Et Astronautica Sinica,2001,22(5):454-457.
[8]Lee B W, Suh J, Lee H, et al. Investigations on Fretting Fatigue in Aircraft Engine Compressor Blade[J].Engineering Failure Analysis, 2011, 18(7):1900-1908.
[9]李康,付雪松,周文龙. 钛合金榫头微动疲劳试验研究现状与发展[J]. 钛工业进展, 2014, 31(4):1-5.
Li Kang, Fu Xuesong, Zhou Wenlong.Present Situation and Development of Titanium Alloy Dovetail Fretting Fatigue Test[J]. Titanium Industry Progress,2014,31(4):1-5.
[10]卫中山,王珉,李亮,等.TC4合金微动疲劳损伤研究[J]. 机械工程材料,2006,30(1):30-32.
Wei Zhongshan, Wang Min, Li Liang, et al. Fretting Fatigue Damage Behavior of TC4 Alloy[J]. Materials for Mechanical Engineering, 2006, 30(1):30-32.
[11]卫中山,王珉,张明,等.TC4钛合金的微动疲劳行为研究[J]. 稀有金属材料与工程,2006,35(7):1050-1052.
Wei Zhongshan, Wang Min, Zhang Ming, et al.Study on Fretting Fatigue Behavior of TC4 Titanium Alloy [J]. Rare Metal Materials and Engineering, 2006,35 (7):1050-1052.
[12]石炜. 航空发动机榫连接结构微动疲劳寿命研究[D]. 南京:南京航空航天大学, 2012.
[13]Golden P J, Nicholas T. The Effect of Angle on Dovetail Fretting Experiments in Ti-6Al-4V[J]. Fatigue & Fracture of Engineering Materials & Structures, 2005, 28:1169-1175.
[14]Golden P J, Calcaterra J R. A Fracture Mechanics Life Prediction Methodology Applied to Dovetail Fretting[J]. Tribology International, 2006, 39(10): 1172-1180.
[15]Rajasekaran R, Nowell D. Fretting Fatigue in Dovetail Blade Roots：Experiment and Analysis[J]. Tribology International, 2006, 39(10):1277-1285.
[16]古远兴, 温卫东, 崔海涛. 高低周载荷作用下燕尾榫结构的微动疲劳寿命预测[J]. 推进技术, 2008,29(2):240-243.
Gu Yuanxing, Wen Weidong,Cui Haitao.Prediction of Fretting Fatigue Life of Dovetail Joint under High-cycle and Low-cycle Load[J]. Journal of Propulsion Technology, 2008,29(2):240-243.
[17]古远兴.高低周复合载荷下燕尾榫结构微动疲劳寿命研究[D].南京:南京航空航天大学, 2007.
[18]Namjoshi S A,Mall S,Jain V K,et al.Fretting Fatigue Crack Initiation Mechanism in Ti–6Al–4V[J].Fatigue & Fracture of Engineering Materials & Structures,2002,25(10):955-964.
[19]周仲荣.关于微动磨损与微动疲劳的研究[J]. 中国机械工程, 2000, 11(10):1146-1150.
Zhou Zhongrong. Study on Fretting Wear and Fretting Fatigue[J]. China Mechanical Engineering, 2000,11(10):1146-1150.
[20]徐小军,刘捍卫,朱旻昊,等.Ti-Al-Zr钛合金的高温微动磨损行为研究[J]. 核动力工程, 2010,31(5):42-47.
Xu Xiaojun, Liu Hanwei, Zhu Minhao, et al. Study on High Temperature Fretting Wear of Ti-Al-Zr Alloy[J].Nuclear Power Engineering, 2010,31(5)：42-47.
[21]Mall S, Kim H K, Saladin E C, et al. Effects of Microstructure on Fretting Fatigue Behavior of IN100[J].Materials Science and Engineering: A, 2010, 527(6): 1453-1460.