摘要/Abstract

摘要：

通过自制的ZL-2型超强脉冲放电装置对含孔洞缺陷的A356铝合金焊接接头进行了电磁热强化实验,采用金相显微镜对强化前后焊接接头各区域微观组织和孔洞附近组织进行了对比分析,利用微机控制万能实验机对强化前后试件的拉伸性能进行了测试，并用SEM扫描电镜对拉伸断口进行了分析，采用型号为FM-700的显微硬度计对强化前后试件进行了硬度测试。结果表明:合适的脉冲电流有较好的晶粒细化效果，强化后的焊接接头各区域组织得到细化，焊接接头的力学性能得到改善，经脉冲放电后的抗拉强度平均提高了11%,延伸率平均提高了14.2%，且强化后接头的硬度明显较强化前高。

关键词: 电磁热强化, 孔洞；焊接接头；A356铝合金

Abstract:

By a ZL-2 super pulse discharge generator,the welded joints of A356 aluminum alloy with hole defects were discharged by electromagnetic heating.Microstructure of welded joints and the microstructure near the hole were analyzed before and after discharge by metallographic microscope.Tensile property test of specimens was made by microcomputer control universal testing machines.Scanning electron microscope was used to observe the fracture organization.Hardness test was made by FM-700 microhardness tester before and after reinforcement.The results show that the appropriate pulse current has better crystal grain refinement effect.After reinforcement the microstructure of welded joints becomes refining,mechanics property of the welding joints is improved,tensile strength is increased 11% and elongation is increased to 14.2% on average after pulse current experiments,and the hardness of welded joints increases obviously.

Key words: electromagnetic , heating;hole defect;welded joint;A356 aluminum alloy

中图分类号:

O346

付宇明, 宋炳材, 李艳芳, 郑丽娟. 含孔洞缺陷焊接接头电磁热强化及组织与性能分析[J]. 中国机械工程, 2015, 26(20): 2811-2815.

Fu Yuming, Song Bingcai, Li Yanfang, Zheng Lijuan. Electromagnetic Heat Strengthening and Microstructure and Properties of Welded Joints with Hole Defects[J]. China Mechanical Engineering, 2015, 26(20): 2811-2815.

参考文献

[1]Wang Q G.Micro-structural Effects on the Tensile and Fracture Behavior of Aluminum Casting Alloys A356/357[J].Metallurgical and Materials Transactions, 2003, 34(12):2887-2899.
[2]Atxaga G,Pelayo A,Irisarri A M.Effect of Microstructure on Fatigue Behaviour of Cast Al-7Si-Mg Alloy[J].Mater. Sci. Tech., 2001, 17 (44) :446- 450.
[3]王恩泽.6082-T6铝合金MIG焊接头微观组织及力学性能的研究[D].吉林：吉林大学，2013.
[4]郑丽娟,向龙,刘会莹,等.异种钢焊接接头脉冲放电强化与力学性能分析[J].中国机械工程,2012, 23(12):1492-1495.
Zheng Lijuan,Xiang Long,Liu Huiying,et al.Pulse Current Discharge for Strengthening Welded Joints of Dissimilar Steel and Analysis of Mechanical Properties[J].China Mechanical Engineering,2012,23(12):1492-1495.
[5]付宇明,郑丽娟,何大川,等.45钢焊接接头电磁热强化及力学性能分析[J].焊接学报,2008, 29(5):5-8.
Fu Yuming,Zheng Lijuan,He Dachuan,et al. Strengthening of Welded Joint of 45 Steel by Electromagnetic Heat Effect and Mechanical Its Performance Analysis[J].Transactions of the China Welding Institution,2008,29(5):5-8.
[6]张洪潮,于静,郝胜智,等.电磁场的热效应在再制造毛坯裂纹止裂中的应用[J].中国机械工程, 2013, 49(7):21-28.
Zhang Hongchao,Yu Jing,Hao Shengzhi,et al.Application of Electro-magnetic Heat Effect on Arresting the Crack in Remanufacturing Blank[J].China Mechanical Engineering,2013, 49(7):21-28.
[7]郑丽娟,周红梅,刘会莹,等.含埋藏孔洞缺陷金属构件电磁热止裂强化分析[J].中国机械工程,2012,23 (11):1285-1288.
Zheng Lijuan,Zhou Hongmei,Liu Huiying,et al.Analysis on Crack Arresting and Strengthening of Metal Structures with Embedding Hole Defects by Using Electromagnetic Heating[J].China Mechanical Engineering,2012,23 (11):1285-1288.

[1]	郝智彦;黄志勇;王清远. 不锈钢焊接件低周疲劳固有耗散分析[J]. 中国机械工程, 2020, 31(17): 2045-2050.
[2]	彭艳;李浩然;刘洋. 考虑平均剪应力效应的纯扭疲劳强度预测[J]. 中国机械工程, 2020, 31(04): 396-402.
[3]	刘俭辉1;吕鑫1;韦尧兵1;程金辉2. 考虑附加强化效应及平均应变的多轴疲劳寿命预估[J]. 中国机械工程, 2020, 31(03): 314-320.
[4]	程里朋1;平学成1,2;王春光1;郭倩1. 纤维金属层板铆接剩余强度影响因素研究[J]. 中国机械工程, 2019, 30(19): 2319-2328.
[5]	闫少文;屈文忠;肖黎. 一种基于高频频响函数的无基准疲劳裂纹识别方法[J]. 中国机械工程, 2019, 30(12): 1428-1432,1479.
[6]	汪必升1;李毅波1,2;廖雅诗3;李剑1. 基于扩展有限元模型的动态应力强度因子计算[J]. 中国机械工程, 2019, 30(11): 1294-1301.
[7]	陈凌1,2;张贤明1;刘飞2;欧阳平1;贾艳艳3. 镁合金非对称应力载荷下的低周疲劳损伤演化和寿命预测[J]. 中国机械工程, 2019, 30(06): 748-755.
[8]	肖俊华1;崔友强1;徐耀玲1;张福成2. 纳米尺度孔边裂纹裂尖Ⅲ型应力强度因子研究[J]. 中国机械工程, 2018, 29(19): 2347-2352.
[9]	安兴强1;谷正气1,2;马骁骙1;张沙1;米承继3. 基于焊缝品质参数区间模型的疲劳寿命预测方法[J]. 中国机械工程, 2017, 28(21): 2639-2645.
[10]	陈亚军, 刘波, 刘辰辰, 周剑. 2A12航空铝合金多轴疲劳试验及应力准则寿命预测模型研究[J]. 中国机械工程, 2017, 28(09): 1092-1096,1100.
[11]	陈凌, 张贤明, 刘飞, 欧阳平, 贾艳艳. 镁合金低周疲劳寿命预测模型探讨[J]. 中国机械工程, 2017, 28(05): 512-518.
[12]	申杰斌, 唐东林. 一种考虑应力梯度的疲劳寿命预测方法[J]. 中国机械工程, 2017, 28(01): 40-44.
[13]	李文凯, 崔海涛, 温卫东, 苏旭明, C C Engler-Pinto Jr. 环境湿度对铸铝合金超声疲劳裂纹扩展速率的影响研究[J]. 中国机械工程, 2016, 27(17): 2396-2401.
[14]	陈凌, 张贤明, 刘飞, 欧阳平, 刘先斌. 一种基于熵增理论的疲劳-蠕变交互作用损伤模型及试验验证[J]. 中国机械工程, 2016, 27(10): 1393-1398.
[15]	李国永, 谷正气, 张, 沙, 马骁骙, 李吉平, 胡楷. 基于不等间距灰色模型的疲劳寿命预测方法[J]. 中国机械工程, 2015, 26(24): 3267-3274.