Erosion Wear Mechanism and Laser Cladding Remanufacturing of High-pressure Throttle Valves

Bo Jikang

Ningbo Polytechnic,Ningbo,Zhejiang,315800

Online:2015-01-25 Published:2015-01-23

摘要/Abstract

摘要：

为获取高压节流阀的冲蚀磨损机理并解决其现场应用中的阀芯局部损伤修复问题,进行了高压节流阀的冲蚀磨损试验。在分析冲蚀磨损现象和形貌的基础上，提出了高压节流阀阀芯的冲蚀磨损机理。为恢复高压节流阀阀芯的服役性能，采用铁基合金粉末进行了阀芯的激光熔覆再制造，恢复了阀芯的形状尺寸。再制造阀芯的冲蚀磨损试验结果表明,激光熔覆再制造可恢复高压节流阀的服役性能。

关键词: 高压节流阀, 冲蚀磨损, 激光熔覆再制造；铁基合金粉末

Abstract:

To solve the problem of erosion wear mechanism and the partial damage repair problems of the valve core in the application of high-pressure throttle valves, this paper performed erosion wear experiments of a high-pressure throttle valve. The erosion wear mechanism of the valve core was presented based on the analysis of erosion phenomena and pattern. To recover the service performance of high-pressure throttle valve, laser cladding remanufacturing of the valve
core was conducted by using ferroalloy powder, and the shape and size of the valve core was restored.The erosion wear experiments of the remanufactured high-pressure throttle valve were performed,and the experimental results show that laser cladding remanufacturing can restore the service performance of the high-pressure throttle valve.

Key words: high-pressure throttle valve, erosion wear, laser cladding remanufacturing, ferroalloy powder

中图分类号:

TH137.5

薄纪康. 高压节流阀的冲蚀磨损机理及其激光熔覆再制造[J]. 中国机械工程, 2015, 26(2): 255-259.

Bo Jikang. Erosion Wear Mechanism and Laser Cladding Remanufacturing of High-pressure Throttle Valves[J]. China Mechanical Engineering, 2015, 26(2): 255-259.

参考文献

[1]王德玉,刘绘新,何霞.高压自控液动恒压节流阀的设计[J].石油机械,2005,33(4):19-20.
Wang Deyu,Liu Huixin,He Xia.High Pressure Self-control Hydrodynamic Throttle Valve[J].China Petroleum Machinery, 2005,33(4)：19-20.
[2]张传涛,单代伟,栾金堂,等.高压板式节流阀流固耦合分析[J].石油机械,2007,35(10)：37-39.
Zhang Chuantao,Shan Daiwei,Luan Jintang,et al.Fluid-solid Coupling Analysis of High-pressure Orifice Choke Valve[J]. China Petroleum Machinery,2007,35(10)：37-39.
[3]王德玉,刘清友,何霞.高压节流阀的失效与受力分析[J].天然气工业,2005,25(6)：1-3.
Wang Deyu, Liu Qingyou,He Xia.Analysis on Failure and Force of High Pressure Throttle Valve[J].Natural Gas Industry, 2005,25(6)：1-3.
[4]丁泽良，李剑峰，邓建新，等.水煤浆喷嘴热冲蚀磨损机理研究[J].摩擦学学报，2003，23(5)：441-444.
Ding Zeliang，Li Jianfeng，Deng Jianxin，et al.Thermal Erosion Wear Behavior of Nozzles in Coal Water Slurry Burning[J]. Tribology，2003，23(5)：441-444.
[5]成细洋，邱长军，张彦.激光熔覆再制造对试件拉伸性能与组织的影响[J].热加工工艺，2012，41(6)：93-99.
Cheng Xiyang，Qiu Changjun，Zhang Yan.The Influence of Laser Cladding Remanufacturing on Tensile Properties and Organization of Specimen[J].Hot Working Technology，2012，41(6)：93-99.
[6]徐滨士，董世运，朱胜史，等.再制造成形技术发展及展望[J].机械工程学报，2012，48(15)：96-105.
Xu Binshi，Dong Shiyun，Zhu Shengshi，et al.Prospects and Developing of Remanufacture Forming Technology[J]. Journal of Mechanical Engineering，2012，48(15)：96-105.
[7]Tan Guangyu，Liu Guangjun，Li Guanghui.Adhesive Failure of Grooved Tool in Milling of 3Cr-1Mo-1/4V Steel[J]. International Journal of Materials & Product Technology，2011，42(3/4)：219-233.
[8]Tan Guangyu,Liu Guangjun,Li Guanghui.Experimental Study on Adhesive Wear of Milling Insert with Complex Groove[J]. International Journal of Advanced Manufacturing Technology,2009,44(7/8)：631-637.
[9]蔡军.基于FGH95镍基高温合金粉末的激光修复基础工艺研究[D].南京：南京航空航天大学，2010.
[10]黄海鸿,刘儒军,张曦,等.面向驱动桥壳再制造的磁记忆无损检测[J].中国机械工程,2013,24(11):1505-1509.
Huang Haihong,Liu Rujun,Zhang Xi,et al.Magnetic Memory Non-destructive Testing(NDT) for Remanufacturing of Drive Axle Housing[J].China Mechanical Engineering,2013,24(11):1505-1509.