中国机械工程 ›› 2010, Vol. 21 ›› Issue (02): 196-201.

改善钛合金切削加工性的置氢工艺及置氢量优化

危卫华1;徐九华1;傅玉灿1;侯红亮2;李志强2

1.南京航空航天大学,南京,210016

2.北京航空制造工程研究所,北京,100024

出版日期:2010-01-25 发布日期:2010-01-28
基金资助:
国家自然科学基金资助项目(50775115)
National Natural Science Foundation of China（No. 50775115）

Optimization of Hydrogenation Process and Hydrogenation Concentration in Improving Titanium Alloy Machinability

Wei Weihua1;Xu Jiuhua1;Fu Yucan1;Hou Hongliang2;Li Zhiqiang2

1.Nanjing University of Aeronautics and Astronautics,Nanjing,210016

2.Beijing Aeronautical Manufacturing Technology Research Institute,Beijing,

100024

Online:2010-01-25 Published:2010-01-28
Supported by:
National Natural Science Foundation of China（No. 50775115）

摘要/Abstract

摘要：

为了改善钛合金的切削加工性能,提出将钛合金进行置氢处理后再进行切削加工。在650℃、750℃和800℃下对Ti-6Al-4V合金进行了置氢处理,并在干切削条件下对其开展了切削力、切削温度对比试验。结果表明：在置氢工艺相同时,随着置氢量增加,热电偶的热电势系数越来越大;主切削力在650℃置氢时相对未置氢试件仅降低2%,750℃置氢时没有降低,而800℃置氢时主切削力约下降了8%;切削温度均呈现先快速降低、经过一平缓变化段后又快速增加的变化趋势,在650℃、750℃和800℃置氢情况下,切削温度相对未置氢试件分别约降低了50℃、76℃和80℃。最终确定优选的置氢工艺为：在800℃下置氢、保温6h、随炉冷却至室温;最佳置氢量范围为0.21%~0.37%。

关键词:

钛合金, 置氢工艺, 置氢量, 热电势系数, 切削力, 切削温度

Abstract:

The titanium alloy is a kind of typical difficult-to-cut material.Before machining,the titanium alloys were processed at 650℃,750℃ and 800℃ by thermohydrogen treatment technology respectively in order to improve the machinability.The measurement experiments about cutting force and cutting temperature were carried out in dry cutting.The results show that, when the hydrogenation process is identical, thermoelectromotive force coefficient increases with the increase of hydrogen concentration.When the Ti-6Al-4V alloy was hydrogenated at 650℃,750℃ and 800℃ respectively,the main cutting force falls 2%,0% and 8% respectively.Moreover,the cutting temperature firstly rapidly reduces,secondly flatly changes,thirdly rapidly increses with the increase of hydrogen concentration, and the cutting temperature reduces 50℃,76℃ and 80℃ respectively under the three hydrogenation temperature.The preferred hydrogenation process of Ti-6Al-4V is as follows,the process is concluded at 800℃ for 6 hours,then cooled in the furnace, and the optimum hydrogen concentration ranges from 0.21% to 0.37%.

Key words: titanium alloy, hydrogenation process, hydrogenation concentration, thermoelectromotive force coefficient, cutting force, cutting temperature

中图分类号:

TG506

危卫华, 徐九华, 傅玉灿, 侯红亮, 李志强.

改善钛合金切削加工性的置氢工艺及置氢量优化

[J]. 中国机械工程, 2010, 21(02): 196-201.

WEI Wei-Hua, XU Jiu-Hua, FU Yu-Can, HOU Gong-Liang, LI Zhi-Jiang.

Optimization of Hydrogenation Process and Hydrogenation Concentration in Improving Titanium Alloy Machinability

[J]. China Mechanical Engineering, 2010, 21(02): 196-201.

参考文献

[1]张喜燕,赵永庆,白晨光编著.钛合金及应用[M],2005:306.
[2]苏宇[1],何宁[1],李亮[1],李新龙[1],赵威[1].低温氮气射流对钛合金高速铣削加工性能的影响[J].中国机械工程,2006,17(11):1183-1187.
[3]张春江主编.钛合金切削加工技术[M].西安:西北工业大学出版社,1986:158.
[4]Ezugwu E O,Bonney J, Yamane Y. An Overview of the Machinahility of Aeroengine Alloys[J]. Journal of Materials Processing Technology, 2003,134 (2) : 233-253.
[5]Leyens C,Peters M.钛与钛合金[M].陈振华,译.北京:化学工业出版社,2005.
[6]Ezugwu E O, Bonney J, Machado A R. The Effect of Argonenriched Environment in High- speed Machining of Titanium Alloy [J]. Tribology Transactions, 2005,48(1) : 18-23.
[7]Kolachev B A, liyin A A, Nosov V K. Hydrogen Technology as New Perspective Type of Titanium Alloy Processing[C]//Advances in the Science and Technology of Titanium Alloy Processing/ Proceedings of an International Symposium held at 125th TMS Annual Meeting and Exhibition. Anaheim, 1996 : 331-338.
[8]侯红亮,李志强,王亚军,关桥.钛合金热氢处理技术及其应用前景[J].中国有色金属学报,2003,13(3):533-549.
[9]Kolachev B A, Talalaev V D, Egorova Y B, et al. Effect of Hydrogen on the Machinability of VT5--1 Alloy by Cutting[J]. Materials Science, 1996 (6): 753-759.
[10]Kolachev B A, Mitin B B, Talalaev V D. Hydrogen Technology of Titanium Alloys [ J ]. Aviation Manufacturing, 1991 (1): 58-59.
[11]Egorova Y B, Iiyin A A, Kolachev B A. Effect of the Structure on the Cutability of Titanium Alloys [J]. Metal Science and Heat Treatment, 2003,45 (3/4) : 134-139.
[12]Froes F H,Senkov O N, Qazi J I. Hydrogen as a Temporary Alloying Element in Titanium Alloys: Thermohydrogen Processing [J]. International Materials Reviews,2004,49(3/4):227-245.
[13]Senkov O N, Froes F H. Thermohydrogen Processing of Titanium Alloys [J]. International Journal of Hydrogen Energy,1999,24(6) :565-576.
[14]林宗涵编著.热力学与统计物理学[M].北京:北京大学出版社,2007:637.
[15]黄泽铣编著.热电偶原理及其检定[M],1993:300.
[16]Martorell I A,Gurney F J,Kerr W R. Pilot Plant Forging of Hydrogenated Ti -- 6A1 -- 4V, ADA089107 [ R], Pittsburgh: Air Force Wright Aeronautical Laboratories, 1980.
[17]Zhao J W, Ding Y, Zhao W J, et al. Influence of Hydrogenation on Microstructures and Microhardness of Ti6A14V Alloy[J]. Transactions of Nonferrous Metals Society of China, 2008, 18 (3) :506-511.