基于汽车驱动桥壳再制造的堆焊可靠性研究

中国机械工程 ›› 2013, Vol. 24 ›› Issue (5): 676-680.

基于汽车驱动桥壳再制造的堆焊可靠性研究

沈晔超1;宋守许1;王玉琳1;杜长春2

1.合肥工业大学，合肥，230009
2.合肥美桥汽车传动及底盘系统有限公司，合肥，230051

出版日期:2013-03-10 发布日期:2013-03-19
基金资助:
国家重点基础研究发展计划(973计划)资助项目(2011CB013406,2011CB013402)；“十一五”国家科技支撑计划资助项目(2008BAC46B01)
National Program on Key Basic Research Project (973 Program)（No. 2011CB013406,2011CB013402）;
The National Key Technology R&D Program（No. 2008BAC46B01）

Reliability of Welded Surfacing Layer for Remanufacture of Vehicle's Drive Axle Housing

Shen Yechao1;Song Shouxu1;Wang Yulin1;Du Changchun2

1.Hefei University of Technology,Hefei,230009
2.Hefei AAM Automotive Driveline & Chassis System Co., Ltd.,Hefei,230051

Online:2013-03-10 Published:2013-03-19
Supported by:

National Program on Key Basic Research Project (973 Program)（No. 2011CB013406,

2011CB013402）;
The National Key Technology R&D Program（No. 2008BAC46B01）

摘要/Abstract

摘要：

为了研究汽车驱动桥壳表面损伤后的堆焊修复层能否满足再制造的要求，选用H13CrMoA和ER50-6焊丝并采用亚激光瞬间熔工艺，在汽车驱动桥壳片表面制备不同厚度的堆焊层。利用金属磁记忆检测仪和扫描电镜分析堆焊试样的应力分布和断面组织特征，同时测试堆焊试样的硬度并进行渗透、磁粉和X射线三种无损检测。结果表明：ER50-6堆焊试样的堆焊层与母材硬度相近，母材热影响区未发生局部软化，堆焊层与母材结合良好，不存在焊接缺陷和应力集中区，应力分布不均匀程度低于H13CrMoA堆焊试样。


关键词: 再制造, 堆焊, 无损检测, 应力分布

Abstract:

In order to discuss whether the welded surfacing layer can satisfy the remanufacture conditions when the surface of vehicle drive axle housing was damaged, the weld surfacing layers with different thicknesses were covered on the surface of drive axle housing shells by using H13CrMoA and ER50-6 with sub-melt laser instantaneous technology. The stress distribution of welding specimens was measured by magnetic memory testing device, the characteristics of this section was analyzed by SEM. The hardness was tested and nondestructive testing was made by osmosis, magnetic powder and X-ray. The testing results indicate that ER50-6 welding specimens has the similar hardness with base metal, the heat affected zone of base metal will not be softened partly. Welded surfacing layer is combined well with base metal. Welding defects and stress concentration do not appear. The uneven distribution of stress is less than the H13CrMoA surfacing specimens. 

Key words: remanufacture, welded surfacing layer, nondestructive test, stress distribution

中图分类号:

TH162

沈晔超1, 宋守许1, 王玉琳1, 杜长春2. 基于汽车驱动桥壳再制造的堆焊可靠性研究[J]. 中国机械工程, 2013, 24(5): 676-680.

CHEN Ye-Chao-1, SONG Shou-Hu-1, WANG Yu-Lin-1, DU Chang-Chun-2. Reliability of Welded Surfacing Layer for Remanufacture of Vehicle's Drive Axle Housing[J]. China Mechanical Engineering, 2013, 24(5): 676-680.

参考文献

[1]刘毅. 东风EQ140汽车后桥壳的修复工艺[J]. 汽车技术，1993(1)：43-47.
Liu Yi. The Repair Technology of Automobile Rear Axle Housing of Dongfeng EQ140[J]. Automobile Technology，1993(1)：43-47.
[2]徐滨士，朱邵华. 表面工程的理论与技术[M]. 北京：国防工业出版社，2010.
[3]杨可，余圣甫，杨华. 氮合金化堆焊硬面合金组织与耐高温磨损性能[J]. 焊接学报，2011，32(1)：5-8.
Yang Ke，Yu Shengfu，Yang Hua. Microstructure and High-temperature Wear-resistance of Nitrogen-alloying Hardfacing Alloy[J]. Transactions of the China Welding，2011，32(1)：5-8.
[4]龚建勋，肖逸锋，马蓦. 过共晶高硼堆焊合金的显微组织及耐磨性[J]. 材料工程，2011(4)：89-93.
Gong Jianxun，Xiao Yifeng，Ma Mo. Microstructure and Abrasion Resistance of Hypereutectic High-boron Hardfacing Alloys[J]. Journal of Materials Engineering，2011(4)：89-93.
[5]刘政军，宋兴奎，唐兴涛. 异种材质堆焊层组织及耐磨性[J]. 焊接学报，2011，32(4)：99-102.
Liu Zhengjun，Song Xingkui，Tang Xingtao. Microstructure and Wear Resistance of Dissimilar Metal Surfacing Layer[J]. Transactions of the China Welding Institution，2011，32(4)：99-102.
[6]Padovani C,Davenport A J,Connolly B J，et al. Corrosion Protection of AA7449-T7951 Friction Stir Welds by Laser Surface Melting with an Excimer Laser[J]. Corrosion Science，2011，53(12)：3956-3969.
[7]Santa J F，Blanco J A，Giraldo J E，et al. Cavitation Erosion of Martensitic and Austenitic Stainless Steel Welded Coatings[J]. Wear，2011，271(9/10)：1445-1453.
[8]Mosallaee P M，Bodaqhi F，Moshrefifar M. Surface Modification of Low Carbon Steel Substrate by Al-rich Clad Layer Applied by GTAW[J]. Surface and Coatings Technology，2011，206(2/3)：217-223.
[9]Sokolov M，Salminen A，Kuznetsov M，et al. Laser Welding and Weld Hardness Analysis of Thick Section S355 Structural Steel[J]. Materials and Design，2011，32(10)：5127-5131.
[10]苏允海，唐兴涛，宋兴奎，等. 异种材质堆焊渗透裂纹和气孔形成机理[J]. 焊接学报，2011，32(6)：97-100.
Su Yunhai，Tang Xingtao，Song Xingkui，et al. Mechanism of Penetrating Crack and Gas Porosity on Dissimilar Metal Surfacing[J]. Transactions of the China Welding Institution，2011，32(6)：97-100.
[11]谢国乔. 16MnL汽车大梁板冷成型开裂的影响因素[J]. 湖南冶金，2006，34(2)：11-16.
Xie Guoqiao.Effect Factors of Cracking During Cold Forming of 16MnL Automobile Frame Steel Plate[J]. Hunan Metallurgy，2006，34(2)：11-16.
[12]章彬斌，梁斌. 基于金属磁记忆方法的压力容器对接焊缝应力检测[J]. 无损检测，2011，33(3)：31-36.
Zhang Binbin，Liang Bin. Stress Inspection of Pressure Vessel Butt Weld Based on Metal Magnetic Memory Technique[J]. Nondestructive Testing，2011，33(3)：31-36.

[1]	李方义, 戚小霞, 李燕乐, 王黎明, 杜际雨, 许京伟, 孟晓宁. 盾构机关键零部件再制造修复技术综述[J]. 中国机械工程, 2021, 32(07): 820-831.
[2]	吴英龙, 宣海军, 单晓明, 付汝龙. 离心轮内部疲劳裂纹扩展及其无损定量表征[J]. 中国机械工程, 2021, 32(06): 658-665.
[3]	宋守许;郁炯. 考虑疲劳损伤的支撑辊主动再制造时机决策方法[J]. 中国机械工程, 2021, 32(05): 565-571.
[4]	袁久鑫;秦训鹏;张进朋;汪小凯. 基于激光超声的电弧增材制件内部缺陷深度检测[J]. 中国机械工程, 2021, 32(01): 65-73.
[5]	宋守许1,2;胡孟成1,2;杜毅1,2;罗润东1,2. 混合定子铁心再制造电机应变数值仿真与转矩不平衡分析[J]. 中国机械工程, 2020, 31(09): 1080-1088.
[6]	杜彦斌1;曹华军2. 基于监测诊断的在役机床个性化再设计技术体系[J]. 中国机械工程, 2020, 31(05): 567-575.
[7]	郭楠1;马喜强1;殷咸青2;余永健1. 基于初始变形的薄板堆焊变形预测技术[J]. 中国机械工程, 2020, 31(03): 367-372.
[8]	宋守许;李诺楠;杜毅;刘涛. 抑制永磁同步电机转矩脉动的转子再设计方法[J]. 中国机械工程, 2019, 30(17): 2084-2090,2134.
[9]	田明明1;解社娟1,2;韩捷3,4;李鹏2;裴翠祥1;陈振茂1. 基于小波分析的脉冲涡流/电磁超声复合无损检测方法[J]. 中国机械工程, 2019, 30(16): 1925-1930.
[10]	李方义1，2;李振1，2;王黎明1，2;李剑峰1，2;李燕乐1，2;鹿海洋1，2;商建通1，2. 内燃机增材再制造修复技术综述[J]. 中国机械工程, 2019, 30(09): 1119-1127,1133.
[11]	柯庆镝;李杰;吕岩;刘光复;宋守许. 基于结构和性能相似度分析函数的机械产品优化设计方法[J]. 中国机械工程, 2019, 30(05): 586-594.
[12]	柯庆镝1;田常俊1;李杰1;李柏青2;翟正树2;詹伟1. 基于表面质量需求的机械零件再制造毛坯预处理工艺优化方法[J]. 中国机械工程, 2018, 29(23): 2859-2866.
[13]	宋守许, 汪伟, 柯庆镝, 邱权. [绿色设计]基于零件结构耦合关系的主动再制造设计方法[J]. 中国机械工程, 2018, 29(21): 2521-2526,2538.
[14]	张洪潮, 李明政, 刘伟嵬, 原应春. [机械装备再制造]机械装备再制造的重点基础科学问题研究综述[J]. 中国机械工程, 2018, 29(21): 2581-2589.
[15]	朱胜, 周超极, 周克兵. [机械装备再制造]绿色增材再制造技术[J]. 中国机械工程, 2018, 29(21): 2590-2593,2614.