中国机械工程 ›› 2021, Vol. 32 ›› Issue (16): 2002-2007,2015.DOI: 10.3969/j.issn.1004-132X.2021.16.013

• 工程前沿 • 上一篇    下一篇

基于固结磨粒的单晶蓝宝石自旋转磨削加工方法

吴柯1;陆新明1;MEHMOOD Awais1;周立波2;袁巨龙3   

  1. 1.宁波大学机械工程与力学学院,宁波,315000
    2.茨城大学工学院,日立,316-8511
    3.浙江工业大学超精密加工中心,杭州,310014
  • 出版日期:2021-08-25 发布日期:2021-09-10
  • 作者简介:吴柯,男,1989年生,讲师。研究方向为硬脆半导体衬底晶片磨削加工技术。发表论文10篇。E-mail:wuke1@nbu.edu.cn。
  • 基金资助:
    国家自然科学基金(51905280);
    宁波市自然科学基金(2019A610153);
    宁波市科技创新2025重大专项(2018B10004)

Fixed Abrasive Based Self-rotation Grinding for Single Crystal Sapphire

WU Ke1;LU Xinming1;MEHMOOD Awais1;ZHOU Libo2;YUAN Julong3   

  1. 1.Faculty of Mechanical Engineering and Mechanics,Ningbo University,Ningbo,Zhejiang,315000
    2.School of Engineering,Ibaraki University,Hitachi,Japan,316-8511
    3.Ultra-precision Machining Center,Zhejiang University of Technology,Hangzhou,310014
  • Online:2021-08-25 Published:2021-09-10

摘要: 利用固结磨粒自旋转磨削加工方法,通过金刚石磨削和化学机械磨削实现了蓝宝石晶片的高效、高质量平坦化加工。采用不同磨粒粒径的金刚石砂轮实现了蓝宝石晶片较高的材料去除率或较好的表面质量。开发了高磨粒浓度Cr2O3砂轮,采用化学机械磨削对金刚石磨削后的蓝宝石晶片进行平坦化加工。实验结果表明,化学机械磨削能够去除金刚石磨削的表面和亚表面缺陷,最终获得表面粗糙度Ra<1 nm、无/微损伤的蓝宝石晶片。通过理论分析单颗金刚石磨粒的磨削力,发现磨粒粒径是影响材料去除率和表面质量的主要影响因素。通过XPS分析证明了Cr2O3和蓝宝石之间的固相反应过程。

关键词: 金刚石磨削, 化学机械磨削, 表面质量, 材料去除率

Abstract: A planarization method was presented for sapphire substrate with high quality and efficiency by applying fixed abrasive based diamond and chemo-mechanical grinding on self-rotation grinding platform. Diamond grinding wheel with different abrasive sizes was able to either obtain faster material removal rate or better surface quality. Then, high Cr2O3 abrasive concentrated wheel was developed, and chemo-mechanical grinding was applied for the planarization processes of sapphire substrate. Experimental result suggests that chemo-mechanical grinding is able to remove the surface and subsurface damages left by diamond grinding. The obtained sapphire substrate is with surface quality Ra less than 1 nm and no/little subsurface damages. Theoretical analysis to the grinding forces for single diamond particle reveals that particle size is the most influential factor on material removal rate and surface quality. The solid phase reaction between Cr2O3 and sapphire was demonstrated by XPS analysis.

Key words: diamond grinding, chemo-mechanical grinding, surface quality, material removal rate