Research on Failure Mechanism of Super-high Pressure Crystal Vessel

Abstract

Abstract:

Though material tensile test,fracture and fatigue tests, hardness test and microstructure analysis for deactivated crystal reactor vessel,the maximum stress and deformation were obtained in danger zone at the bottom crystal vessel by finite

element method and the rupture strength and fatigue life of crystal vessel were also analyzed and calculated.Combining the analyses about stress corrosion, corrosion fatigue and creep deformation,it is pointed out that the failure of crystal vessel is a brittle fracture under the co-activation between corrosion fatigue and creep.

Key words:

crystal vessel, fatigue, creep, corrosion, material deterioration

摘要：

对失效水晶釜釜体材料进行了拉伸试验、断裂与疲劳性能试验、硬度测试和金相分析，利用有限元法求得了水晶釜底部危险区域的最大应力和变形，分析计算了水晶釜的断裂强度和疲劳寿命。结合对水晶釜应力腐蚀、腐蚀疲劳和蠕变变形等的分析，指出了水晶釜的失效为腐蚀疲劳和蠕变调和作用下的脆性断裂。

关键词:

水晶釜, 疲劳, 蠕变, 腐蚀, 材质劣化



CLC Number:

TG111.91

LIU Kang-Lin, ZHANG Jing-Wei, GONG Chao.

Research on Failure Mechanism of Super-high Pressure Crystal Vessel

[J]. China Mechanical Engineering, 2011, 22(8): 914-916.

刘康林, 张经伟, 公涛.

超高压水晶釜的失效机理研究

[J]. 中国机械工程, 2011, 22(8): 914-916.

[1]	WANG Rong, LI Junjie, ZHENG Wenge, WANG Jia, HE Mingrong. Gear Fatigue Damage Prediction with Coupling Effect of Environmental Randomness and Load Sequence [J]. China Mechanical Engineering, 2026, 37(1): 105-113.
[2]	YU Changrui, LIU Liangbao, ZHOU Jinggang, ZHANG Han, HUANG Dong, ZHANG Ning, LI Xun. Optimization of Roller Burnishing Parameters for Concave Circular-arc Surfaces of Turbine Disk Mortise Grooves [J]. China Mechanical Engineering, 2026, 37(1): 60-65.
[3]	Lingyun YAO, Zhishun YANG, Li LI, Yongjie LIN. Research on Load Spectrum Editing Based on Optimal Pseudo Wigner-Ville Distribution Method [J]. China Mechanical Engineering, 2025, 36(11): 2501-2508.
[4]	Hongwei LIU, Renke KANG, Xianglong ZHU, Haotian MU, Fangzhou HE, Mo CHEN. Improvement of Fatigue Performances of AISI 4340 Steel Thread Root by Rolling Processes [J]. China Mechanical Engineering, 2025, 36(10): 2241-2248.
[5]	Xingyu WANG, Yanbao GUO, Zheng ZHANG, Zhangyu QIAO, Fa GAO, Jinzhong CHEN, Chang LIU. Research on Vibration Fatigue of Pipeline Inspection Gauge Sealing Discs under Influences of Pipeline Defects [J]. China Mechanical Engineering, 2025, 36(10): 2292-2299.
[6]	Huiming YANG, Xia YANG, Yuqi HUANG. Full-cycle Fatigue Life Prediction of Rolling Bearings Based on Paris Modeling [J]. China Mechanical Engineering, 2025, 36(09): 2003-2010.
[7]	Jinyu ZHOU, Yifei CHEN. Prediction of Fatigue Property of SLM Metal Parts Based on Multi-scale Simulations [J]. China Mechanical Engineering, 2025, 36(09): 2087-2096.
[8]	Sizhu ZHOU, Qiongyao XIANG, Yun ZENG. Fatigue Cumulative Damage Model Considering Dynamic Memory Properties of Materials [J]. China Mechanical Engineering, 2025, 36(08): 1740-1748.
[9]	Qingwang ZHU, Jing ZHANG, Faxiang XIE, Zhonggang ZHU, Jianyu GUO, Houlin YAN. Design and Experimental Research of RV Reducer Main Bearing Test Benches [J]. China Mechanical Engineering, 2025, 36(08): 1749-1756.
[10]	JIANG Shijie1, 2, CAI Shanggang1, YING Hongwei1, CHEN Jiaqi1. Fatigue Property of 17-4PH Products Fabricated via Metal Material Extrusion Technique [J]. China Mechanical Engineering, 2025, 36(07): 1582-1591.
[11]	YANG Yu1, 2, LI Xiaolei2, TAO Yourui1, 2, GUO Qiyu1, 2, YE Nan1, 2. Accelerated Load Spectrum Preparation for RV Reducer Service Conditions [J]. China Mechanical Engineering, 2025, 36(06): 1170-1177.
[12]	NIU Yanzhao1, LIU Hongwei1, SONG Yali2, ZHU Xianglong1, HUANG Jiamei2, KANG Renke1. Optimization and Experimental Study of Bolt Retreat Groove Rolling Wheels Based on Finite Element Simulation [J]. China Mechanical Engineering, 2025, 36(06): 1214-1221.
[13]	TAN Liang1, 2, FAN Yi3, YAO Changfeng1, 2. Investigation on Evolution Laws for Surface States of TC17 Alloy Induced by UIT during High-cycle Fatigue at 400 ℃ [J]. China Mechanical Engineering, 2025, 36(04): 790-801.
[14]	WANG Chi1, 2, ZHOU Yu1, 2, WENG Zhiyi1, 2. Reconstruction of Magnetic Field Responses Caused by Rail Surface Cracks with Alternative Current Excitation [J]. China Mechanical Engineering, 2025, 36(04): 830-839.
[15]	LIU Yang1, WEN Zefeng1, WU Xingwen2, ZHOU Yabo1, TAO Gongquan1, ZHANG Zhenxian3, HOU Jianwen3, YI Zhi4. Fatigue Failure Study and Topology Optimization of Metro Vehicle Cowcatchers Based on Virtual Excitation Method [J]. China Mechanical Engineering, 2025, 36(04): 840-849.