Weld Formation of High Strength Steels by Low-power Pulsed Laser Induced Mental Active Gas Hybrid Welding in Overhead Positions

doi:10.3969/j.issn.1004-132X.2020.17.017

Abstract

Abstract: A low-power pulsed laser induced metal active gas(MAG) arc hybrid welding tests in overhead positions were carried out for 5mm thick E36 high strength steel plates. The results show that heat input of laser induced MAG arc hybrid welding is 29% lower than that of single arc welding. By reducing weld pool sizes, hybrid welding may effectively inhibit the formation of concave defects, and then increase the processsing parameter ranges. Tensile tests and bending tests show that the welding joints without internal concave defects have good static tensile strength and bending load. Static tensile strength of the welding joints with internal concave is equivalent to the base metal, but the maximum bending load is significantly reduced.

Key words: impulse laser welding, arc welding, high strength steel, overhead position welding, mechanics property

摘要： 针对5 mm厚E36高强钢板材，开展了低功率脉冲激光诱导熔化极活性气体保护电弧复合仰焊试验。研究结果表明：相比于熔化极活性气体保护电弧焊，激光诱导熔化极活性气体保护电弧复合焊接接头的焊接热输入可降低29%。复合焊接通过减小焊接熔池尺寸，可有效抑制内凹缺陷的产生，进而增大工艺参数区间。拉伸和弯曲试验表明，无内凹缺陷接头具有良好抗拉强度和弯曲载荷；有内凹缺陷接头抗拉强度与母材相当，但最大弯曲载荷显著降低。

关键词: 脉冲激光焊, 电弧焊, 高强钢, 仰焊, 力学性能

CLC Number:

TP182

LIU Liming;CHEN Liang;SONG Gang. Weld Formation of High Strength Steels by Low-power Pulsed Laser Induced Mental Active Gas Hybrid Welding in Overhead Positions[J]. China Mechanical Engineering, DOI: 10.3969/j.issn.1004-132X.2020.17.017.

刘黎明;陈亮;宋刚. 高强钢低功率脉冲激光诱导熔化极活性气体保护电弧仰焊成形[J]. 中国机械工程, DOI: 10.3969/j.issn.1004-132X.2020.17.017.

References

[1]许宁，王峰会，罗金恒，等. X80管线钢焊接接头TEM观察下的断裂行为对比[J].中国机械工程，2016，27(3)：403-407.
XU Ning, WANG Fenghui, LUO Jinheng, et al. Comparison of Fracture Behaviors of X80 Pipeline Steel Welded Joints under TEM Observasion[J].China Mechanical Engineering, 2016, 27(3): 403-407.
[2]陈彦宾，冯杰才，李俐群，等. 高强钢厚板激光-GMAW复合双面同步横焊特性研究[J]. 机械工程学报，2016，52(2)：47-55.
CHEN Yanbin, FENG Jiecai, LI Liqun, et al. Research on the Characteristics of Double-sided Hybrid Laser-GMAW Synchronous Horizontal Welding of High-strength Thick Steel Plates[J]. Journal of Mechanical Engineering, 2016, 52(2): 47-55.
[3]岳建锋，李亮玉，姜旭东，等. 全位置MAG焊缝成形控制技术及研究进展[J]. 中国机械工程，2012，23(10)：1256-1259.
YUE Jianfeng, LI Liangyu, JIANG Xudong, et al. All Position MAG Welding Formation Control Technology and Research Review[J].China Mechanical Engineering，2012，23(10)：1256-1259.
[4]郭春富，孙伟强，刘帛炎，等. 管道全位置自动焊的研究现状及展望[J]. 电焊机，2017(11)：87-91.
GUO Chunfu, SUN Weiqiang, LIU Boyan, et al. Research Status and Expectation on All Position Automatic Welding for Pipeline[J]. Welding Machine，2017(11): 87-91.
[5]陈树君，卢振洋，任福深，等. 管道全位置自动焊机的专用电源及焊接工艺[J]. 焊接学报，2009，30(2)：13-16．
CHEN Shujun, LU Zhenyang, REN Fushen，et al. Special Welding Machine and Welding Process for All Position Automatic Pipeline Welding[J]. Transactions of the China Welding Institution，2009，30(2)：13-16.
[6]FERNNDEZ TAVITAS R J，SALDAA GARCS R, LPEZ CORTZ V H. Hybrid Laser Arc Welding Applied in Longitudinal Joints for Hydrocarbon Conduction Pipes[J].MRS Proceedings，2015，1766：45-52.
[7]TURICHIN G，KUZNETSOV M，SOKOLOV M，et al. Hybrid Laser Arc Welding of X80 Steel Influence of Welding Speed and Preheating on the Microstructure and Mechanical Properties[J]. Physics Procedia，2015，78：35-44.
[8]雷正龙，檀财旺，陈彦宾，等. X80管线钢光纤激光-MAG复合焊接打底层组织及性能[J].中国激光，2013，40(4): 74-80.
LEI Zhenglong，TAN Caiwang，CHEN Yanbin，et al. Microstructure and Mechanical Properties of X80 Pipeline Steel Backing Welded Joint by Fiber Laser-MAG Hybrid Weld[J]. Chinese J. Lasers，2013，40(4)：74-80.
[9]曾惠林，张元，皮亚东，等. 长输管道激光-电弧复合焊接技术研究[J]. 焊接与切割，2017(4)：10-13.
ZENG Huilin，ZHANG Yuan，PI Yadong，et al. Research on Laser-arc Hybrid Welding for Long Distance Transportation Pipeline[J].Welding and Cutting，2017(4)：10-13.
[10]刘黎明，王红阳，宋刚. 能源节约型激光诱导电弧复合焊技术及应用[J]. 焊接学报，2015(11)：9-12.
LIU Liming，WANG Hongyang，SONG Gang. Energy-saving Mode Laser Induced Arc Hybrid Welding Technology and Application[J].Transactions of the China Welding Institution，2015，36(11)：9-12.
[11]HU B，OUDEN G D. Synergetic Effects of Hybrid Laser-arc Welding[J].Science and Technology of Welding & Joining，2005，10(4)：427-431.
[12]HAN Y Q，GUO L，CHEN S J，et al. Weld Formation Stability and Force in Variable Polarity Plasma Arc Keyhole Welding[J]. Journal of Materials Engineering，2011,1(12)：83-86.

[1]	Changhong GUO, Mengran DI, Hanwen GONG, Lingxiao QUAN, Bin LI. Modeling of Aviation Fuel Pipe Welds in Different Regions and Its Effect on Mechanics Properties of Pipes [J]. China Mechanical Engineering, 2025, 36(09): 1916-1924.
[2]	Xudong WANG, Jing ZHAO. Research on Contact Properties of Clamp-Shear-Grab Integrated Attachments under Self-locked States [J]. China Mechanical Engineering, 2025, 36(09): 2117-2125.
[3]	WANG Yahui1, 2, 3, HUANG Liang1, 2, LIU Xiang1, 2. Effects of Solution Treatment on Microstructure and Mechanics Properties of TC4 Titanium Alloy Parts Formed by Forging/Additive Manufacturing Composite Forming [J]. China Mechanical Engineering, 2025, 36(06): 1314-1321.
[4]	MO Shuai1, 2, 3, HUANG Xuan1, 2, HUANG Zurui1, 2, ZHANG Wei1. Continuous Multi-stable Gear Cell Mechanical Metastructures and Mechanics Properties [J]. China Mechanical Engineering, 2025, 36(04): 857-863，887.
[5]	JIANG Shijie1, 2, XU Zizhao1, LI Shuguang1, WANG Fei1, HUANG Xuzhen3. Study on Forming and Mechanics Properties of 17-4PH Stainless Steel Parts Fabricated by MFFF Technique [J]. China Mechanical Engineering, 2025, 36(03): 593-603.
[6]	CHENG Aiguo1, WANG Chao1, YU Wanyuan2, HE Zhicheng1. Numerical and Experimental Study on Effects of Rivet Crack on Mechanics Properties of Self-piercing Riveted Joints [J]. China Mechanical Engineering, 2025, 36(02): 197-208.
[7]	WAN Buyan1, 2, PENG Fenfei1, 2, 3, JIN Yongping1, 2, LIU Deshun1, 2, PENG Youduo1, 2. A Review of Mechanics Property Studies of Retracting and Releasing Cables for Marine Exploration Equipment [J]. China Mechanical Engineering, 2024, 35(09): 1521-1533.
[8]	ZHANG Wukun1, 2, ZHAO Jian2, TAN Yonghua1, 2, GAO Yushan1, 2, WANG Jun1, 2, HAN Ziyue3, GENG Xiaoliang4. Analysis of Compressive Mechanics Properties of Body Centered Cubic Lattice with Pillars in Different Reinforcement Directions and Their Filling Structures [J]. China Mechanical Engineering, 2024, 35(09): 1642-1652.
[9]	NI Jing, CUI Zhi, HE Lihua, FU Xin, ZHU Zefei. State-of-the-Art of Cutting Technology and Applications of PTFE [J]. China Mechanical Engineering, 2024, 35(03): 498-514.
[10]	YUE Jianfeng, LONG Xinyu, HUANG Yunlong, GUO Jialong, LIU Wenji. On-line Identification of Narrow Gap P-GMAW Sidewall Fusion States Based on Arc Acoustic Signals [J]. China Mechanical Engineering, 2024, 35(02): 244-250，259.
[11]	ZHANG Wenjun, WANG Wenqi, ZHANG Xiaodong, LIN Wei, ZHANG Yandong, BAI Zhenhua, . Comprehensive Thickness Control Technology of 1180 MPa Grade Ultra-high Strength Steels in Cold Tandem Rolling [J]. China Mechanical Engineering, 2024, 35(02): 347-353，370.
[12]	TWANG Wei, MA Qianlun, BAI Zhenhua, WANG Ziang. Mechanics Property Prediction of Cold Rolled High Strength Steel Coils Based on GBD#br# [J]. China Mechanical Engineering, 2023, 34(18): 2222-2229.
[13]	LIU Ying, CHEN Yue, ZHAO Xueli, YU Tongmin, ZHU Tieli, . Study on Properties of Ultrasonic-assisted Injection Molding of Carbon Fiber-reinforced Polypropylene Parts [J]. China Mechanical Engineering, 2023, 34(16): 1975-1981.
[14]	LI Guangjun, DUAN Hong, XU Lei, KAN Chen, LIU Zhongliang, GAO Xiaodong. Research on Friction and Wear Behaviors of Al7.8Co20.6Cr12.2Fe11.5Ni40.7Ti7.2 High-entropy Superalloy [J]. China Mechanical Engineering, 2023, 34(13): 1568-1575.
[15]	ZHOU Houming, CHEN Haoyue, LI Shengui. Preparation and Mechanics Properties of Al2O3/ZrO2 Ceramic Tool Materials Based on Gradient Structure [J]. China Mechanical Engineering, 2023, 34(10): 1199-1207.